--- interfacial/interfacial.tex 2011/07/14 21:36:07 3740 +++ interfacial/interfacial.tex 2011/07/28 20:25:08 3754 @@ -73,31 +73,28 @@ Interfacial thermal conductance is extensively studied %%%%%%%%%%%%%%%%%%%%%%%%%%%%%%%%%%%%%%%%%%%%%%%%%%%%%%%%%%%%%%%%%%%%%%%%%%%%%%% \section{Introduction} -Interfacial thermal conductance is extensively studied both -experimentally and computationally\cite{cahill:793}, due to its -importance in nanoscale science and technology. Reliability of -nanoscale devices depends on their thermal transport -properties. Unlike bulk homogeneous materials, nanoscale materials -features significant presence of interfaces, and these interfaces -could dominate the heat transfer behavior of these -materials. Furthermore, these materials are generally heterogeneous, -which challenges traditional research methods for homogeneous -systems. +Due to the importance of heat flow in nanotechnology, interfacial +thermal conductance has been studied extensively both experimentally +and computationally.\cite{cahill:793} Unlike bulk materials, nanoscale +materials have a significant fraction of their atoms at interfaces, +and the chemical details of these interfaces govern the heat transfer +behavior. Furthermore, the interfaces are +heterogeneous (e.g. solid - liquid), which provides a challenge to +traditional methods developed for homogeneous systems. -Heat conductance of molecular and nano-scale interfaces will be -affected by the chemical details of the surface. Experimentally, -various interfaces have been investigated for their thermal -conductance properties. Wang {\it et al.} studied heat transport -through long-chain hydrocarbon monolayers on gold substrate at -individual molecular level\cite{Wang10082007}; Schmidt {\it et al.} -studied the role of CTAB on thermal transport between gold nanorods -and solvent\cite{doi:10.1021/jp8051888}; Juv\'e {\it et al.} studied +Experimentally, various interfaces have been investigated for their +thermal conductance. Wang {\it et al.} studied heat transport through +long-chain hydrocarbon monolayers on gold substrate at individual +molecular level,\cite{Wang10082007} Schmidt {\it et al.} studied the +role of CTAB on thermal transport between gold nanorods and +solvent,\cite{doi:10.1021/jp8051888} and Juv\'e {\it et al.} studied the cooling dynamics, which is controlled by thermal interface resistence of glass-embedded metal -nanoparticles\cite{PhysRevB.80.195406}. Although interfaces are -commonly barriers for heat transport, Alper {\it et al.} suggested -that specific ligands (capping agents) could completely eliminate this -barrier ($G\rightarrow\infty$)\cite{doi:10.1021/la904855s}. +nanoparticles.\cite{PhysRevB.80.195406} Although interfaces are +normally considered barriers for heat transport, Alper {\it et al.} +suggested that specific ligands (capping agents) could completely +eliminate this barrier +($G\rightarrow\infty$).\cite{doi:10.1021/la904855s} Theoretical and computational models have also been used to study the interfacial thermal transport in order to gain an understanding of @@ -105,18 +102,22 @@ atoms)\cite{hase:2010,hase:2011}. However, ensemble av employed Non-Equilibrium Molecular Dynamics (NEMD) simulations to study thermal transport from hot Au(111) substrate to a self-assembled monolayer of alkylthiol with relatively long chain (8-20 carbon -atoms)\cite{hase:2010,hase:2011}. However, ensemble averaged +atoms).\cite{hase:2010,hase:2011} However, ensemble averaged measurements for heat conductance of interfaces between the capping -monolayer on Au and a solvent phase has yet to be studied. -The comparatively low thermal flux through interfaces is +monolayer on Au and a solvent phase have yet to be studied with their +approach. The comparatively low thermal flux through interfaces is difficult to measure with Equilibrium MD or forward NEMD simulation -methods. Therefore, the Reverse NEMD (RNEMD) methods would have the -advantage of having this difficult to measure flux known when studying -the thermal transport across interfaces, given that the simulation -methods being able to effectively apply an unphysical flux in -non-homogeneous systems. +methods. Therefore, the Reverse NEMD (RNEMD) +methods\cite{MullerPlathe:1997xw,kuang:164101} would have the +advantage of applying this difficult to measure flux (while measuring +the resulting gradient), given that the simulation methods being able +to effectively apply an unphysical flux in non-homogeneous systems. +Garde and coworkers\cite{garde:nl2005,garde:PhysRevLett2009} applied +this approach to various liquid interfaces and studied how thermal +conductance (or resistance) is dependent on chemistry details of +interfaces, e.g. hydrophobic and hydrophilic aqueous interfaces. -Recently, we have developed the Non-Isotropic Velocity Scaling (NIVS) +Recently, we have developed a Non-Isotropic Velocity Scaling (NIVS) algorithm for RNEMD simulations\cite{kuang:164101}. This algorithm retains the desirable features of RNEMD (conservation of linear momentum and total energy, compatibility with periodic boundary @@ -131,30 +132,30 @@ underlying mechanism for this phenomena was investigat properties. Different models were used for both the capping agent and the solvent force field parameters. Using the NIVS algorithm, the thermal transport across these interfaces was studied and the -underlying mechanism for this phenomena was investigated. +underlying mechanism for the phenomena was investigated. -[MAY ADD WHY STUDY AU-THIOL SURFACE; CITE SHAOYI JIANG] - \section{Methodology} \subsection{Imposd-Flux Methods in MD Simulations} -For systems with low interfacial conductivity one must have a method -capable of generating relatively small fluxes, compared to those -required for bulk conductivity. This requirement makes the calculation -even more difficult for those slowly-converging equilibrium -methods\cite{Viscardy:2007lq}. -Forward methods impose gradient, but in interfacail conditions it is -not clear what behavior to impose at the boundary... - Imposed-flux reverse non-equilibrium -methods\cite{MullerPlathe:1997xw} have the flux set {\it a priori} and -the thermal response becomes easier to -measure than the flux. Although M\"{u}ller-Plathe's original momentum -swapping approach can be used for exchanging energy between particles -of different identity, the kinetic energy transfer efficiency is -affected by the mass difference between the particles, which limits -its application on heterogeneous interfacial systems. +Steady state MD simulations have an advantage in that not many +trajectories are needed to study the relationship between thermal flux +and thermal gradients. For systems with low interfacial conductance, +one must have a method capable of generating or measuring relatively +small fluxes, compared to those required for bulk conductivity. This +requirement makes the calculation even more difficult for +slowly-converging equilibrium methods.\cite{Viscardy:2007lq} Forward +NEMD methods impose a gradient (and measure a flux), but at interfaces +it is not clear what behavior should be imposed at the boundaries +between materials. Imposed-flux reverse non-equilibrium +methods\cite{MullerPlathe:1997xw} set the flux {\it a priori} and +the thermal response becomes an easy-to-measure quantity. Although +M\"{u}ller-Plathe's original momentum swapping approach can be used +for exchanging energy between particles of different identity, the +kinetic energy transfer efficiency is affected by the mass difference +between the particles, which limits its application on heterogeneous +interfacial systems. -The non-isotropic velocity scaling (NIVS)\cite{kuang:164101} approach to -non-equilibrium MD simulations is able to impose a wide range of +The non-isotropic velocity scaling (NIVS) \cite{kuang:164101} approach +to non-equilibrium MD simulations is able to impose a wide range of kinetic energy fluxes without obvious perturbation to the velocity distributions of the simulated systems. Furthermore, this approach has the advantage in heterogeneous interfaces in that kinetic energy flux @@ -171,61 +172,34 @@ momenta and energy and does not depend on an external for computing thermal conductivities. The NIVS algorithm conserves momenta and energy and does not depend on an external thermostat. -\subsection{Defining Interfacial Thermal Conductivity $G$} -For interfaces with a relatively low interfacial conductance, the bulk -regions on either side of an interface rapidly come to a state in -which the two phases have relatively homogeneous (but distinct) -temperatures. The interfacial thermal conductivity $G$ can therefore -be approximated as: +\subsection{Defining Interfacial Thermal Conductivity ($G$)} + +For an interface with relatively low interfacial conductance, and a +thermal flux between two distinct bulk regions, the regions on either +side of the interface rapidly come to a state in which the two phases +have relatively homogeneous (but distinct) temperatures. The +interfacial thermal conductivity $G$ can therefore be approximated as: \begin{equation} -G = \frac{E_{total}}{2 t L_x L_y \left( \langle T_\mathrm{hot}\rangle - + G = \frac{E_{total}}{2 t L_x L_y \left( \langle T_\mathrm{hot}\rangle - \langle T_\mathrm{cold}\rangle \right)} \label{lowG} \end{equation} -where ${E_{total}}$ is the imposed non-physical kinetic energy -transfer and ${\langle T_\mathrm{hot}\rangle}$ and ${\langle - T_\mathrm{cold}\rangle}$ are the average observed temperature of the -two separated phases. +where ${E_{total}}$ is the total imposed non-physical kinetic energy +transfer during the simulation and ${\langle T_\mathrm{hot}\rangle}$ +and ${\langle T_\mathrm{cold}\rangle}$ are the average observed +temperature of the two separated phases. When the interfacial conductance is {\it not} small, there are two -ways to define $G$. - -One way is to assume the temperature is discrete on the two sides of -the interface. $G$ can be calculated using the applied thermal flux -$J$ and the maximum temperature difference measured along the thermal -gradient max($\Delta T$), which occurs at the Gibbs deviding surface, -as: +ways to define $G$. One common way is to assume the temperature is +discrete on the two sides of the interface. $G$ can be calculated +using the applied thermal flux $J$ and the maximum temperature +difference measured along the thermal gradient max($\Delta T$), which +occurs at the Gibbs deviding surface (Figure \ref{demoPic}): \begin{equation} -G=\frac{J}{\Delta T} + G=\frac{J}{\Delta T} \label{discreteG} \end{equation} -The other approach is to assume a continuous temperature profile along -the thermal gradient axis (e.g. $z$) and define $G$ at the point where -the magnitude of thermal conductivity $\lambda$ change reach its -maximum, given that $\lambda$ is well-defined throughout the space: -\begin{equation} -G^\prime = \Big|\frac{\partial\lambda}{\partial z}\Big| - = \Big|\frac{\partial}{\partial z}\left(-J_z\Big/ - \left(\frac{\partial T}{\partial z}\right)\right)\Big| - = |J_z|\Big|\frac{\partial^2 T}{\partial z^2}\Big| - \Big/\left(\frac{\partial T}{\partial z}\right)^2 -\label{derivativeG} -\end{equation} - -With the temperature profile obtained from simulations, one is able to -approximate the first and second derivatives of $T$ with finite -difference methods and thus calculate $G^\prime$. - -In what follows, both definitions have been used for calculation and -are compared in the results. - -To compare the above definitions ($G$ and $G^\prime$), we have modeled -a metal slab with its (111) surfaces perpendicular to the $z$-axis of -our simulation cells. Both with and withour capping agents on the -surfaces, the metal slab is solvated with simple organic solvents, as -illustrated in Figure \ref{demoPic}. - \begin{figure} \includegraphics[width=\linewidth]{method} \caption{Interfacial conductance can be calculated by applying an @@ -240,82 +214,116 @@ With the simulation cell described above, we are able \label{demoPic} \end{figure} +The other approach is to assume a continuous temperature profile along +the thermal gradient axis (e.g. $z$) and define $G$ at the point where +the magnitude of thermal conductivity ($\lambda$) change reaches its +maximum, given that $\lambda$ is well-defined throughout the space: +\begin{equation} +G^\prime = \Big|\frac{\partial\lambda}{\partial z}\Big| + = \Big|\frac{\partial}{\partial z}\left(-J_z\Big/ + \left(\frac{\partial T}{\partial z}\right)\right)\Big| + = |J_z|\Big|\frac{\partial^2 T}{\partial z^2}\Big| + \Big/\left(\frac{\partial T}{\partial z}\right)^2 +\label{derivativeG} +\end{equation} + +With temperature profiles obtained from simulation, one is able to +approximate the first and second derivatives of $T$ with finite +difference methods and calculate $G^\prime$. In what follows, both +definitions have been used, and are compared in the results. + +To investigate the interfacial conductivity at metal / solvent +interfaces, we have modeled a metal slab with its (111) surfaces +perpendicular to the $z$-axis of our simulation cells. The metal slab +has been prepared both with and without capping agents on the exposed +surface, and has been solvated with simple organic solvents, as +illustrated in Figure \ref{gradT}. + With the simulation cell described above, we are able to equilibrate the system and impose an unphysical thermal flux between the liquid and the metal phase using the NIVS algorithm. By periodically applying -the unphysical flux, we are able to obtain a temperature profile and -its spatial derivatives. These quantities enable the evaluation of the -interfacial thermal conductance of a surface. Figure \ref{gradT} is an -example how those applied thermal fluxes can be used to obtain the 1st -and 2nd derivatives of the temperature profile. +the unphysical flux, we obtained a temperature profile and its spatial +derivatives. Figure \ref{gradT} shows how an applied thermal flux can +be used to obtain the 1st and 2nd derivatives of the temperature +profile. \begin{figure} \includegraphics[width=\linewidth]{gradT} -\caption{The 1st and 2nd derivatives of temperature profile can be - obtained with finite difference approximation.} +\caption{A sample of Au-butanethiol/hexane interfacial system and the + temperature profile after a kinetic energy flux is imposed to + it. The 1st and 2nd derivatives of the temperature profile can be + obtained with finite difference approximation (lower panel).} \label{gradT} \end{figure} \section{Computational Details} \subsection{Simulation Protocol} The NIVS algorithm has been implemented in our MD simulation code, -OpenMD\cite{Meineke:2005gd,openmd}, and was used for our -simulations. Different slab thickness (layer numbers of Au) were -simulated. Metal slabs were first equilibrated under atmospheric -pressure (1 atm) and a desired temperature (e.g. 200K). After -equilibration, butanethiol capping agents were placed at three-fold -sites on the Au(111) surfaces. The maximum butanethiol capacity on Au -surface is $1/3$ of the total number of surface Au -atoms\cite{vlugt:cpc2007154}. A series of different coverages was -investigated in order to study the relation between coverage and -interfacial conductance. +OpenMD\cite{Meineke:2005gd,openmd}, and was used for our simulations. +Metal slabs of 6 or 11 layers of Au atoms were first equilibrated +under atmospheric pressure (1 atm) and 200K. After equilibration, +butanethiol capping agents were placed at three-fold hollow sites on +the Au(111) surfaces. These sites are either {\it fcc} or {\it + hcp} sites, although Hase {\it et al.} found that they are +equivalent in a heat transfer process,\cite{hase:2010} so we did not +distinguish between these sites in our study. The maximum butanethiol +capacity on Au surface is $1/3$ of the total number of surface Au +atoms, and the packing forms a $(\sqrt{3}\times\sqrt{3})R30^\circ$ +structure\cite{doi:10.1021/ja00008a001,doi:10.1021/cr9801317}. A +series of lower coverages was also prepared by eliminating +butanethiols from the higher coverage surface in a regular manner. The +lower coverages were prepared in order to study the relation between +coverage and interfacial conductance. The capping agent molecules were allowed to migrate during the simulations. They distributed themselves uniformly and sampled a number of three-fold sites throughout out study. Therefore, the -initial configuration would not noticeably affect the sampling of a +initial configuration does not noticeably affect the sampling of a variety of configurations of the same coverage, and the final conductance measurement would be an average effect of these -configurations explored in the simulations. [MAY NEED FIGURES] +configurations explored in the simulations. -After the modified Au-butanethiol surface systems were equilibrated -under canonical ensemble, organic solvent molecules were packed in the -previously empty part of the simulation cells\cite{packmol}. Two +After the modified Au-butanethiol surface systems were equilibrated in +the canonical (NVT) ensemble, organic solvent molecules were packed in +the previously empty part of the simulation cells.\cite{packmol} Two solvents were investigated, one which has little vibrational overlap -with the alkanethiol and a planar shape (toluene), and one which has -similar vibrational frequencies and chain-like shape ({\it n}-hexane). +with the alkanethiol and which has a planar shape (toluene), and one +which has similar vibrational frequencies to the capping agent and +chain-like shape ({\it n}-hexane). -The space filled by solvent molecules, i.e. the gap between -periodically repeated Au-butanethiol surfaces should be carefully -chosen. A very long length scale for the thermal gradient axis ($z$) -may cause excessively hot or cold temperatures in the middle of the +The simulation cells were not particularly extensive along the +$z$-axis, as a very long length scale for the thermal gradient may +cause excessively hot or cold temperatures in the middle of the solvent region and lead to undesired phenomena such as solvent boiling or freezing when a thermal flux is applied. Conversely, too few solvent molecules would change the normal behavior of the liquid phase. Therefore, our $N_{solvent}$ values were chosen to ensure that -these extreme cases did not happen to our simulations. And the -corresponding spacing is usually $35 \sim 60$\AA. +these extreme cases did not happen to our simulations. The spacing +between periodic images of the gold interfaces is $45 \sim 75$\AA. -The initial configurations generated by Packmol are further -equilibrated with the $x$ and $y$ dimensions fixed, only allowing -length scale change in $z$ dimension. This is to ensure that the -equilibration of liquid phase does not affect the metal crystal -structure in $x$ and $y$ dimensions. Further equilibration are run -under NVT and then NVE ensembles. +The initial configurations generated are further equilibrated with the +$x$ and $y$ dimensions fixed, only allowing the $z$-length scale to +change. This is to ensure that the equilibration of liquid phase does +not affect the metal's crystalline structure. Comparisons were made +with simulations that allowed changes of $L_x$ and $L_y$ during NPT +equilibration. No substantial changes in the box geometry were noticed +in these simulations. After ensuring the liquid phase reaches +equilibrium at atmospheric pressure (1 atm), further equilibration was +carried out under canonical (NVT) and microcanonical (NVE) ensembles. -After the systems reach equilibrium, NIVS is implemented to impose a -periodic unphysical thermal flux between the metal and the liquid -phase. Most of our simulations are under an average temperature of -$\sim$200K. Therefore, this flux usually comes from the metal to the +After the systems reach equilibrium, NIVS was used to impose an +unphysical thermal flux between the metal and the liquid phases. Most +of our simulations were done under an average temperature of +$\sim$200K. Therefore, thermal flux usually came from the metal to the liquid so that the liquid has a higher temperature and would not -freeze due to excessively low temperature. This induced temperature -gradient is stablized and the simulation cell is devided evenly into -N slabs along the $z$-axis and the temperatures of each slab are -recorded. When the slab width $d$ of each slab is the same, the -derivatives of $T$ with respect to slab number $n$ can be directly -used for $G^\prime$ calculations: -\begin{equation} -G^\prime = |J_z|\Big|\frac{\partial^2 T}{\partial z^2}\Big| +freeze due to lowered temperatures. After this induced temperature +gradient had stablized, the temperature profile of the simulation cell +was recorded. To do this, the simulation cell is devided evenly into +$N$ slabs along the $z$-axis. The average temperatures of each slab +are recorded for 1$\sim$2 ns. When the slab width $d$ of each slab is +the same, the derivatives of $T$ with respect to slab number $n$ can +be directly used for $G^\prime$ calculations: \begin{equation} + G^\prime = |J_z|\Big|\frac{\partial^2 T}{\partial z^2}\Big| \Big/\left(\frac{\partial T}{\partial z}\right)^2 = |J_z|\Big|\frac{1}{d^2}\frac{\partial^2 T}{\partial n^2}\Big| \Big/\left(\frac{1}{d}\frac{\partial T}{\partial n}\right)^2 @@ -324,123 +332,137 @@ G^\prime = |J_z|\Big|\frac{\partial^2 T}{\partial z^2} \label{derivativeG2} \end{equation} +All of the above simulation procedures use a time step of 1 fs. Each +equilibration stage took a minimum of 100 ps, although in some cases, +longer equilibration stages were utilized. + \subsection{Force Field Parameters} -Our simulations include various components. Therefore, force field -parameter descriptions are needed for interactions both between the -same type of particles and between particles of different species. +Our simulations include a number of chemically distinct components. +Figure \ref{demoMol} demonstrates the sites defined for both +United-Atom and All-Atom models of the organic solvent and capping +agents in our simulations. Force field parameters are needed for +interactions both between the same type of particles and between +particles of different species. -The Au-Au interactions in metal lattice slab is described by the -quantum Sutton-Chen (QSC) formulation\cite{PhysRevB.59.3527}. The QSC -potentials include zero-point quantum corrections and are -reparametrized for accurate surface energies compared to the -Sutton-Chen potentials\cite{Chen90}. - -Figure \ref{demoMol} demonstrates how we name our pseudo-atoms of the -organic solvent molecules in our simulations. - \begin{figure} \includegraphics[width=\linewidth]{structures} \caption{Structures of the capping agent and solvents utilized in these simulations. The chemically-distinct sites (a-e) are expanded in terms of constituent atoms for both United Atom (UA) and All Atom (AA) force fields. Most parameters are from - Refs. \protect\cite{TraPPE-UA.alkanes,TraPPE-UA.alkylbenzenes} (UA) and - \protect\cite{OPLSAA} (AA). Cross-interactions with the Au atoms are given - in Table \ref{MnM}.} + Refs. \protect\cite{TraPPE-UA.alkanes,TraPPE-UA.alkylbenzenes,TraPPE-UA.thiols} (UA) and \protect\cite{OPLSAA} (AA). Cross-interactions with the Au atoms are given in Table \ref{MnM}.} \label{demoMol} \end{figure} -For both solvent molecules, straight chain {\it n}-hexane and aromatic -toluene, United-Atom (UA) and All-Atom (AA) models are used -respectively. The TraPPE-UA +The Au-Au interactions in metal lattice slab is described by the +quantum Sutton-Chen (QSC) formulation.\cite{PhysRevB.59.3527} The QSC +potentials include zero-point quantum corrections and are +reparametrized for accurate surface energies compared to the +Sutton-Chen potentials.\cite{Chen90} + +For the two solvent molecules, {\it n}-hexane and toluene, two +different atomistic models were utilized. Both solvents were modeled +using United-Atom (UA) and All-Atom (AA) models. The TraPPE-UA parameters\cite{TraPPE-UA.alkanes,TraPPE-UA.alkylbenzenes} are used -for our UA solvent molecules. In these models, pseudo-atoms are -located at the carbon centers for alkyl groups. By eliminating -explicit hydrogen atoms, these models are simple and computationally -efficient, while maintains good accuracy. However, the TraPPE-UA for -alkanes is known to predict a lower boiling point than experimental -values. Considering that after an unphysical thermal flux is applied -to a system, the temperature of ``hot'' area in the liquid phase would be -significantly higher than the average, to prevent over heating and -boiling of the liquid phase, the average temperature in our -simulations should be much lower than the liquid boiling point. [MORE DISCUSSION] -For UA-toluene model, rigid body constraints are applied, so that the -benzene ring and the methyl-CRar bond are kept rigid. This would save -computational time.[MORE DETAILS] +for our UA solvent molecules. In these models, sites are located at +the carbon centers for alkyl groups. Bonding interactions, including +bond stretches and bends and torsions, were used for intra-molecular +sites closer than 3 bonds. For non-bonded interactions, Lennard-Jones +potentials are used. +By eliminating explicit hydrogen atoms, the TraPPE-UA models are +simple and computationally efficient, while maintaining good accuracy. +However, the TraPPE-UA model for alkanes is known to predict a slighly +lower boiling point than experimental values. This is one of the +reasons we used a lower average temperature (200K) for our +simulations. If heat is transferred to the liquid phase during the +NIVS simulation, the liquid in the hot slab can actually be +substantially warmer than the mean temperature in the simulation. The +lower mean temperatures therefore prevent solvent boiling. + +For UA-toluene, the non-bonded potentials between intermolecular sites +have a similar Lennard-Jones formulation. The toluene molecules were +treated as a single rigid body, so there was no need for +intramolecular interactions (including bonds, bends, or torsions) in +this solvent model. + Besides the TraPPE-UA models, AA models for both organic solvents are -included in our studies as well. For hexane, the OPLS-AA\cite{OPLSAA} -force field is used. [MORE DETAILS] -For toluene, the United Force Field developed by Rapp\'{e} {\it et - al.}\cite{doi:10.1021/ja00051a040} is adopted.[MORE DETAILS] +included in our studies as well. The OPLS-AA\cite{OPLSAA} force fields +were used. For hexane, additional explicit hydrogen sites were +included. Besides bonding and non-bonded site-site interactions, +partial charges and the electrostatic interactions were added to each +CT and HC site. For toluene, a flexible model for the toluene molecule +was utilized which included bond, bend, torsion, and inversion +potentials to enforce ring planarity. -The capping agent in our simulations, the butanethiol molecules can -either use UA or AA model. The TraPPE-UA force fields includes +The butanethiol capping agent in our simulations, were also modeled +with both UA and AA model. The TraPPE-UA force field includes parameters for thiol molecules\cite{TraPPE-UA.thiols} and are used for UA butanethiol model in our simulations. The OPLS-AA also provides parameters for alkyl thiols. However, alkyl thiols adsorbed on Au(111) -surfaces do not have the hydrogen atom bonded to sulfur. To adapt this -change and derive suitable parameters for butanethiol adsorbed on -Au(111) surfaces, we adopt the S parameters from Luedtke and -Landman\cite{landman:1998} and modify parameters for its neighbor C -atom for charge balance in the molecule. Note that the model choice -(UA or AA) of capping agent can be different from the -solvent. Regardless of model choice, the force field parameters for -interactions between capping agent and solvent can be derived using -Lorentz-Berthelot Mixing Rule: +surfaces do not have the hydrogen atom bonded to sulfur. To derive +suitable parameters for butanethiol adsorbed on Au(111) surfaces, we +adopt the S parameters from Luedtke and Landman\cite{landman:1998} and +modify the parameters for the CTS atom to maintain charge neutrality +in the molecule. Note that the model choice (UA or AA) for the capping +agent can be different from the solvent. Regardless of model choice, +the force field parameters for interactions between capping agent and +solvent can be derived using Lorentz-Berthelot Mixing Rule: \begin{eqnarray} -\sigma_{IJ} & = & \frac{1}{2} \left(\sigma_{II} + \sigma_{JJ}\right) \\ -\epsilon_{IJ} & = & \sqrt{\epsilon_{II}\epsilon_{JJ}} + \sigma_{ij} & = & \frac{1}{2} \left(\sigma_{ii} + \sigma_{jj}\right) \\ + \epsilon_{ij} & = & \sqrt{\epsilon_{ii}\epsilon_{jj}} \end{eqnarray} -To describe the interactions between metal Au and non-metal capping -agent and solvent particles, we refer to an adsorption study of alkyl -thiols on gold surfaces by Vlugt {\it et - al.}\cite{vlugt:cpc2007154} They fitted an effective Lennard-Jones -form of potential parameters for the interaction between Au and -pseudo-atoms CH$_x$ and S based on a well-established and widely-used -effective potential of Hautman and Klein\cite{hautman:4994} for the -Au(111) surface. As our simulations require the gold lattice slab to -be non-rigid so that it could accommodate kinetic energy for thermal -transport study purpose, the pair-wise form of potentials is -preferred. +To describe the interactions between metal (Au) and non-metal atoms, +we refer to an adsorption study of alkyl thiols on gold surfaces by +Vlugt {\it et al.}\cite{vlugt:cpc2007154} They fitted an effective +Lennard-Jones form of potential parameters for the interaction between +Au and pseudo-atoms CH$_x$ and S based on a well-established and +widely-used effective potential of Hautman and Klein for the Au(111) +surface.\cite{hautman:4994} As our simulations require the gold slab +to be flexible to accommodate thermal excitation, the pair-wise form +of potentials they developed was used for our study. -Besides, the potentials developed from {\it ab initio} calculations by -Leng {\it et al.}\cite{doi:10.1021/jp034405s} are adopted for the -interactions between Au and aromatic C/H atoms in toluene.[MORE DETAILS] +The potentials developed from {\it ab initio} calculations by Leng +{\it et al.}\cite{doi:10.1021/jp034405s} are adopted for the +interactions between Au and aromatic C/H atoms in toluene. However, +the Lennard-Jones parameters between Au and other types of particles, +(e.g. AA alkanes) have not yet been established. For these +interactions, the Lorentz-Berthelot mixing rule can be used to derive +effective single-atom LJ parameters for the metal using the fit values +for toluene. These are then used to construct reasonable mixing +parameters for the interactions between the gold and other atoms. +Table \ref{MnM} summarizes the ``metal/non-metal'' parameters used in +our simulations. -However, the Lennard-Jones parameters between Au and other types of -particles in our simulations are not yet well-established. For these -interactions, we attempt to derive their parameters using the Mixing -Rule. To do this, the ``Metal-non-Metal'' (MnM) interaction parameters -for Au is first extracted from the Au-CH$_x$ parameters by applying -the Mixing Rule reversely. Table \ref{MnM} summarizes these ``MnM'' -parameters in our simulations. - \begin{table*} \begin{minipage}{\linewidth} \begin{center} - \caption{Non-bonded interaction paramters for non-metal - particles and metal-non-metal interactions in our - simulations.} - - \begin{tabular}{cccccc} + \caption{Non-bonded interaction parameters (including cross + interactions with Au atoms) for both force fields used in this + work.} + \begin{tabular}{lllllll} \hline\hline - Non-metal atom $I$ & $\sigma_{II}$ & $\epsilon_{II}$ & $q_I$ & - $\sigma_{AuI}$ & $\epsilon_{AuI}$ \\ - (or pseudo-atom) & \AA & kcal/mol & & \AA & kcal/mol \\ + & Site & $\sigma_{ii}$ & $\epsilon_{ii}$ & $q_i$ & + $\sigma_{Au-i}$ & $\epsilon_{Au-i}$ \\ + & & (\AA) & (kcal/mol) & ($e$) & (\AA) & (kcal/mol) \\ \hline - CH3 & 3.75 & 0.1947 & - & 3.54 & 0.2146 \\ - CH2 & 3.95 & 0.0914 & - & 3.54 & 0.1749 \\ - CHar & 3.695 & 0.1003 & - & 3.4625 & 0.1680 \\ - CRar & 3.88 & 0.04173 & - & 3.555 & 0.1604 \\ - S & 4.45 & 0.25 & - & 2.40 & 8.465 \\ - CT3 & 3.50 & 0.066 & -0.18 & 3.365 & 0.1373 \\ - CT2 & 3.50 & 0.066 & -0.12 & 3.365 & 0.1373 \\ - CTT & 3.50 & 0.066 & -0.065 & 3.365 & 0.1373 \\ - HC & 2.50 & 0.030 & 0.06 & 2.865 & 0.09256 \\ - CA & 3.55 & 0.070 & -0.115 & 3.173 & 0.0640 \\ - HA & 2.42 & 0.030 & 0.115 & 2.746 & 0.0414 \\ + United Atom (UA) + &CH3 & 3.75 & 0.1947 & - & 3.54 & 0.2146 \\ + &CH2 & 3.95 & 0.0914 & - & 3.54 & 0.1749 \\ + &CHar & 3.695 & 0.1003 & - & 3.4625 & 0.1680 \\ + &CRar & 3.88 & 0.04173 & - & 3.555 & 0.1604 \\ + \hline + All Atom (AA) + &CT3 & 3.50 & 0.066 & -0.18 & 3.365 & 0.1373 \\ + &CT2 & 3.50 & 0.066 & -0.12 & 3.365 & 0.1373 \\ + &CTT & 3.50 & 0.066 & -0.065 & 3.365 & 0.1373 \\ + &HC & 2.50 & 0.030 & 0.06 & 2.865 & 0.09256 \\ + &CA & 3.55 & 0.070 & -0.115 & 3.173 & 0.0640 \\ + &HA & 2.42 & 0.030 & 0.115 & 2.746 & 0.0414 \\ + \hline + Both UA and AA + & S & 4.45 & 0.25 & - & 2.40 & 8.465 \\ \hline\hline \end{tabular} \label{MnM} @@ -449,10 +471,215 @@ parameters in our simulations. \end{table*} -\section{Results and Discussions} -[MAY HAVE A BRIEF SUMMARY] -\subsection{How Simulation Parameters Affects $G$} -[MAY NOT PUT AT FIRST] +\section{Results} +There are many factors contributing to the measured interfacial +conductance; some of these factors are physically motivated +(e.g. coverage of the surface by the capping agent coverage and +solvent identity), while some are governed by parameters of the +methodology (e.g. applied flux and the formulas used to obtain the +conductance). In this section we discuss the major physical and +calculational effects on the computed conductivity. + +\subsection{Effects due to capping agent coverage} + +A series of different initial conditions with a range of surface +coverages was prepared and solvated with various with both of the +solvent molecules. These systems were then equilibrated and their +interfacial thermal conductivity was measured with our NIVS +algorithm. Figure \ref{coverage} demonstrates the trend of conductance +with respect to surface coverage. + +\begin{figure} +\includegraphics[width=\linewidth]{coverage} +\caption{Comparison of interfacial thermal conductivity ($G$) values + for the Au-butanethiol/solvent interface with various UA models and + different capping agent coverages at $\langle T\rangle\sim$200K.} +\label{coverage} +\end{figure} + + +In partially covered butanethiol on the Au(111) surface, the +derivative definition for $G^\prime$ (Eq. \ref{derivativeG}) becomes +difficult to apply, as the location of maximum change of $\lambda$ +becomes washed out. The discrete definition (Eq. \ref{discreteG}) is +easier to apply, as the Gibbs dividing surface is still +well-defined. Therefore, $G$ (not $G^\prime$) was used in this +section. + +From Figure \ref{coverage}, one can see the significance of the +presence of capping agents. When even a small fraction of the Au(111) +surface sites are covered with butanethiols, the conductivity exhibits +an enhancement by at least a factor of 3. This indicates the important +role cappping agents are playing for thermal transport at metal / +organic solvent surfaces. + +We note a non-monotonic behavior in the interfacial conductance as a +function of surface coverage. The maximum conductance (largest $G$) +happens when the surfaces are about 75\% covered with butanethiol +caps. The reason for this behavior is not entirely clear. One +explanation is that incomplete butanethiol coverage allows small gaps +between butanethiols to form. These gaps can be filled by transient +solvent molecules. These solvent molecules couple very strongly with +the hot capping agent molecules near the surface, and can then carry +(diffusively) the excess thermal energy away from the surface. + +There appears to be a competition between the conduction of the +thermal energy away from the surface by the capping agents (enhanced +by greater coverage) and the coupling of the capping agents with the +solvent (enhanced by physical contact at lower coverages). This +competition would lead to the non-monotonic coverage behavior observed +here. + +A comparison of the results obtained from the two different organic +solvents can also provide useful information of the interfacial +thermal transport process. The deuterated hexane (UA) results do not +appear to be substantially different from those of normal hexane (UA), +given that butanethiol (UA) is non-deuterated for both solvents. The +UA models, even though they have eliminated C-H vibrational overlap, +still have significant overlap in the infrared spectra. Because +differences in the infrared range do not seem to produce an observable +difference for the results of $G$ (Figure \ref{uahxnua}). + +\begin{figure} +\includegraphics[width=\linewidth]{uahxnua} +\caption{Vibrational spectra obtained for normal (upper) and + deuterated (lower) hexane in Au-butanethiol/hexane + systems. Butanethiol spectra are shown as reference. Both hexane and + butanethiol were using United-Atom models.} +\label{uahxnua} +\end{figure} + +Furthermore, results for rigid body toluene solvent, as well as other +UA-hexane solvents, are reasonable within the general experimental +ranges\cite{Wilson:2002uq,cahill:793,PhysRevB.80.195406}. This +suggests that explicit hydrogen might not be a required factor for +modeling thermal transport phenomena of systems such as +Au-thiol/organic solvent. + +However, results for Au-butanethiol/toluene do not show an identical +trend with those for Au-butanethiol/hexane in that $G$ remains at +approximately the same magnitue when butanethiol coverage differs from +25\% to 75\%. This might be rooted in the molecule shape difference +for planar toluene and chain-like {\it n}-hexane. Due to this +difference, toluene molecules have more difficulty in occupying +relatively small gaps among capping agents when their coverage is not +too low. Therefore, the solvent-capping agent contact may keep +increasing until the capping agent coverage reaches a relatively low +level. This becomes an offset for decreasing butanethiol molecules on +its effect to the process of interfacial thermal transport. Thus, one +can see a plateau of $G$ vs. butanethiol coverage in our results. + +\subsection{Effects due to Solvent \& Solvent Models} +In addition to UA solvent/capping agent models, AA models are included +in our simulations as well. Besides simulations of the same (UA or AA) +model for solvent and capping agent, different models can be applied +to different components. Furthermore, regardless of models chosen, +either the solvent or the capping agent can be deuterated, similar to +the previous section. Table \ref{modelTest} summarizes the results of +these studies. + +\begin{table*} + \begin{minipage}{\linewidth} + \begin{center} + + \caption{Computed interfacial thermal conductivity ($G$ and + $G^\prime$) values for interfaces using various models for + solvent and capping agent (or without capping agent) at + $\langle T\rangle\sim$200K. (D stands for deuterated solvent + or capping agent molecules; ``Avg.'' denotes results that are + averages of simulations under different $J_z$'s. Error + estimates indicated in parenthesis.)} + + \begin{tabular}{llccc} + \hline\hline + Butanethiol model & Solvent & $J_z$ & $G$ & $G^\prime$ \\ + (or bare surface) & model & (GW/m$^2$) & + \multicolumn{2}{c}{(MW/m$^2$/K)} \\ + \hline + UA & UA hexane & Avg. & 131(9) & 87(10) \\ + & UA hexane(D) & 1.95 & 153(5) & 136(13) \\ + & AA hexane & Avg. & 131(6) & 122(10) \\ + & UA toluene & 1.96 & 187(16) & 151(11) \\ + & AA toluene & 1.89 & 200(36) & 149(53) \\ + \hline + AA & UA hexane & 1.94 & 116(9) & 129(8) \\ + & AA hexane & Avg. & 442(14) & 356(31) \\ + & AA hexane(D) & 1.93 & 222(12) & 234(54) \\ + & UA toluene & 1.98 & 125(25) & 97(60) \\ + & AA toluene & 3.79 & 487(56) & 290(42) \\ + \hline + AA(D) & UA hexane & 1.94 & 158(25) & 172(4) \\ + & AA hexane & 1.92 & 243(29) & 191(11) \\ + & AA toluene & 1.93 & 364(36) & 322(67) \\ + \hline + bare & UA hexane & Avg. & 46.5(3.2) & 49.4(4.5) \\ + & UA hexane(D) & 0.98 & 43.9(4.6) & 43.0(2.0) \\ + & AA hexane & 0.96 & 31.0(1.4) & 29.4(1.3) \\ + & UA toluene & 1.99 & 70.1(1.3) & 65.8(0.5) \\ + \hline\hline + \end{tabular} + \label{modelTest} + \end{center} + \end{minipage} +\end{table*} + +To facilitate direct comparison, the same system with differnt models +for different components uses the same length scale for their +simulation cells. Without the presence of capping agent, using +different models for hexane yields similar results for both $G$ and +$G^\prime$, and these two definitions agree with eath other very +well. This indicates very weak interaction between the metal and the +solvent, and is a typical case for acoustic impedance mismatch between +these two phases. + +As for Au(111) surfaces completely covered by butanethiols, the choice +of models for capping agent and solvent could impact the measurement +of $G$ and $G^\prime$ quite significantly. For Au-butanethiol/hexane +interfaces, using AA model for both butanethiol and hexane yields +substantially higher conductivity values than using UA model for at +least one component of the solvent and capping agent, which exceeds +the general range of experimental measurement results. This is +probably due to the classically treated C-H vibrations in the AA +model, which should not be appreciably populated at normal +temperatures. In comparison, once either the hexanes or the +butanethiols are deuterated, one can see a significantly lower $G$ and +$G^\prime$. In either of these cases, the C-H(D) vibrational overlap +between the solvent and the capping agent is removed (Figure +\ref{aahxntln}). Conclusively, the improperly treated C-H vibration in +the AA model produced over-predicted results accordingly. Compared to +the AA model, the UA model yields more reasonable results with higher +computational efficiency. + +\begin{figure} +\includegraphics[width=\linewidth]{aahxntln} +\caption{Spectra obtained for All-Atom model Au-butanethil/solvent + systems. When butanethiol is deuterated (lower left), its + vibrational overlap with hexane would decrease significantly, + compared with normal butanethiol (upper left). However, this + dramatic change does not apply to toluene as much (right).} +\label{aahxntln} +\end{figure} + +However, for Au-butanethiol/toluene interfaces, having the AA +butanethiol deuterated did not yield a significant change in the +measurement results. Compared to the C-H vibrational overlap between +hexane and butanethiol, both of which have alkyl chains, that overlap +between toluene and butanethiol is not so significant and thus does +not have as much contribution to the heat exchange +process. Conversely, extra degrees of freedom such as the C-H +vibrations could yield higher heat exchange rate between these two +phases and result in a much higher conductivity. + +Although the QSC model for Au is known to predict an overly low value +for bulk metal gold conductivity\cite{kuang:164101}, our computational +results for $G$ and $G^\prime$ do not seem to be affected by this +drawback of the model for metal. Instead, our results suggest that the +modeling of interfacial thermal transport behavior relies mainly on +the accuracy of the interaction descriptions between components +occupying the interfaces. + +\subsection{Effects due to methodology and simulation parameters} + We have varied our protocol or other parameters of the simulations in order to investigate how these factors would affect the measurement of $G$'s. It turned out that while some of these parameters would not @@ -461,14 +688,15 @@ during equilibrating the liquid phase. Due to the stif results. In some of our simulations, we allowed $L_x$ and $L_y$ to change -during equilibrating the liquid phase. Due to the stiffness of the Au -slab, $L_x$ and $L_y$ would not change noticeably after -equilibration. Although $L_z$ could fluctuate $\sim$1\% after a system -is fully equilibrated in the NPT ensemble, this fluctuation, as well -as those comparably smaller to $L_x$ and $L_y$, would not be magnified -on the calculated $G$'s, as shown in Table \ref{AuThiolHexaneUA}. This -insensivity to $L_i$ fluctuations allows reliable measurement of $G$'s -without the necessity of extremely cautious equilibration process. +during equilibrating the liquid phase. Due to the stiffness of the +crystalline Au structure, $L_x$ and $L_y$ would not change noticeably +after equilibration. Although $L_z$ could fluctuate $\sim$1\% after a +system is fully equilibrated in the NPT ensemble, this fluctuation, as +well as those of $L_x$ and $L_y$ (which is significantly smaller), +would not be magnified on the calculated $G$'s, as shown in Table +\ref{AuThiolHexaneUA}. This insensivity to $L_i$ fluctuations allows +reliable measurement of $G$'s without the necessity of extremely +cautious equilibration process. As stated in our computational details, the spacing filled with solvent molecules can be chosen within a range. This allows some @@ -480,6 +708,7 @@ Our NIVS algorithm allows change of unphysical thermal smaller system size would be preferable, given that the liquid phase structure is not affected. +\subsubsection{Effects of applied flux} Our NIVS algorithm allows change of unphysical thermal flux both in direction and in quantity. This feature extends our investigation of interfacial thermal conductance. However, the magnitude of this @@ -495,20 +724,21 @@ $J_z$ is listed in Table \ref{AuThiolHexaneUA} and [RE the thermal flux across the interface. For our simulations, we denote $J_z$ to be positive when the physical thermal flux is from the liquid to metal, and negative vice versa. The $G$'s measured under different -$J_z$ is listed in Table \ref{AuThiolHexaneUA} and [REF]. These -results do not suggest that $G$ is dependent on $J_z$ within this flux -range. The linear response of flux to thermal gradient simplifies our -investigations in that we can rely on $G$ measurement with only a -couple $J_z$'s and do not need to test a large series of fluxes. +$J_z$ is listed in Table \ref{AuThiolHexaneUA} and +\ref{AuThiolToluene}. These results do not suggest that $G$ is +dependent on $J_z$ within this flux range. The linear response of flux +to thermal gradient simplifies our investigations in that we can rely +on $G$ measurement with only a couple $J_z$'s and do not need to test +a large series of fluxes. -%ADD MORE TO TABLE \begin{table*} \begin{minipage}{\linewidth} \begin{center} \caption{Computed interfacial thermal conductivity ($G$ and $G^\prime$) values for the 100\% covered Au-butanethiol/hexane interfaces with UA model and different hexane molecule numbers - at different temperatures using a range of energy fluxes.} + at different temperatures using a range of energy + fluxes. Error estimates indicated in parenthesis.} \begin{tabular}{ccccccc} \hline\hline @@ -517,24 +747,24 @@ couple $J_z$'s and do not need to test a large series (K) & & $L_x$ \& $L_y$? & (g/cm$^3$) & (GW/m$^2$) & \multicolumn{2}{c}{(MW/m$^2$/K)} \\ \hline - 200 & 266 & No & 0.672 & -0.96 & 102() & 80.0() \\ - & 200 & Yes & 0.694 & 1.92 & 129() & 87.3() \\ - & & Yes & 0.672 & 1.93 & 131() & 77.5() \\ - & & No & 0.688 & 0.96 & 125() & 90.2() \\ - & & & & 1.91 & 139() & 101() \\ - & & & & 2.83 & 141() & 89.9() \\ - & 166 & Yes & 0.679 & 0.97 & 115() & 69.3() \\ - & & & & 1.94 & 125() & 87.1() \\ - & & No & 0.681 & 0.97 & 141() & 77.7() \\ - & & & & 1.92 & 138() & 98.9() \\ + 200 & 266 & No & 0.672 & -0.96 & 102(3) & 80.0(0.8) \\ + & 200 & Yes & 0.694 & 1.92 & 129(11) & 87.3(0.3) \\ + & & Yes & 0.672 & 1.93 & 131(16) & 78(13) \\ + & & No & 0.688 & 0.96 & 125(16) & 90.2(15) \\ + & & & & 1.91 & 139(10) & 101(10) \\ + & & & & 2.83 & 141(6) & 89.9(9.8) \\ + & 166 & Yes & 0.679 & 0.97 & 115(19) & 69(18) \\ + & & & & 1.94 & 125(9) & 87.1(0.2) \\ + & & No & 0.681 & 0.97 & 141(30) & 78(22) \\ + & & & & 1.92 & 138(4) & 98.9(9.5) \\ \hline - 250 & 200 & No & 0.560 & 0.96 & 74.8() & 61.8() \\ - & & & & -0.95 & 49.4() & 45.7() \\ - & 166 & Yes & 0.570 & 0.98 & 79.0() & 62.9() \\ - & & No & 0.569 & 0.97 & 80.3() & 67.1() \\ - & & & & 1.44 & 76.2() & 64.8() \\ - & & & & -0.95 & 56.4() & 54.4() \\ - & & & & -1.85 & 47.8() & 53.5() \\ + 250 & 200 & No & 0.560 & 0.96 & 75(10) & 61.8(7.3) \\ + & & & & -0.95 & 49.4(0.3) & 45.7(2.1) \\ + & 166 & Yes & 0.570 & 0.98 & 79.0(3.5) & 62.9(3.0) \\ + & & No & 0.569 & 0.97 & 80.3(0.6) & 67(11) \\ + & & & & 1.44 & 76.2(5.0) & 64.8(3.8) \\ + & & & & -0.95 & 56.4(2.5) & 54.4(1.1) \\ + & & & & -1.85 & 47.8(1.1) & 53.5(1.5) \\ \hline\hline \end{tabular} \label{AuThiolHexaneUA} @@ -542,6 +772,8 @@ Furthermore, we also attempted to increase system aver \end{minipage} \end{table*} +\subsubsection{Effects due to average temperature} + Furthermore, we also attempted to increase system average temperatures to above 200K. These simulations are first equilibrated in the NPT ensemble under normal pressure. As stated above, the TraPPE-UA model @@ -550,7 +782,8 @@ butanethiol as well.[MAY NEED FIGURE] And this reduced temperature is higher than 250K. Additionally, the equilibrated liquid hexane density under 250K becomes lower than experimental value. This expanded liquid phase leads to lower contact between hexane and -butanethiol as well.[MAY NEED FIGURE] And this reduced contact would +butanethiol as well.[MAY NEED SLAB DENSITY FIGURE] +And this reduced contact would probably be accountable for a lower interfacial thermal conductance, as shown in Table \ref{AuThiolHexaneUA}. @@ -565,26 +798,25 @@ in that higher degree of contact could yield increased important role in the thermal transport process across the interface in that higher degree of contact could yield increased conductance. -[ADD ERROR ESTIMATE TO TABLE] \begin{table*} \begin{minipage}{\linewidth} \begin{center} \caption{Computed interfacial thermal conductivity ($G$ and $G^\prime$) values for a 90\% coverage Au-butanethiol/toluene interface at different temperatures using a range of energy - fluxes.} + fluxes. Error estimates indicated in parenthesis.} \begin{tabular}{ccccc} \hline\hline $\langle T\rangle$ & $\rho_{toluene}$ & $J_z$ & $G$ & $G^\prime$ \\ (K) & (g/cm$^3$) & (GW/m$^2$) & \multicolumn{2}{c}{(MW/m$^2$/K)} \\ \hline - 200 & 0.933 & -1.86 & 180() & 135() \\ - & & 2.15 & 204() & 113() \\ - & & -3.93 & 175() & 114() \\ + 200 & 0.933 & 2.15 & 204(12) & 113(12) \\ + & & -1.86 & 180(3) & 135(21) \\ + & & -3.93 & 176(5) & 113(12) \\ \hline - 300 & 0.855 & -1.91 & 143() & 125() \\ - & & -4.19 & 134() & 113() \\ + 300 & 0.855 & -1.91 & 143(5) & 125(2) \\ + & & -4.19 & 135(9) & 113(12) \\ \hline\hline \end{tabular} \label{AuThiolToluene} @@ -616,41 +848,47 @@ above. Our Au-butanethiol/toluene system did not see t However, when the surface is not completely covered by butanethiols, the simulated system is more resistent to the reconstruction -above. Our Au-butanethiol/toluene system did not see this phenomena -even at $\langle T\rangle\sim$300K. The Au(111) surfaces have a 90\% -coverage of butanethiols and have empty three-fold sites. These empty -sites could help prevent surface reconstruction in that they provide -other means of capping agent relaxation. It is observed that +above. Our Au-butanethiol/toluene system had the Au(111) surfaces 90\% +covered by butanethiols, but did not see this above phenomena even at +$\langle T\rangle\sim$300K. The empty three-fold sites not occupied by +capping agents could help prevent surface reconstruction in that they +provide other means of capping agent relaxation. It is observed that butanethiols can migrate to their neighbor empty sites during a simulation. Therefore, we were able to obtain $G$'s for these interfaces even at a relatively high temperature without being affected by surface reconstructions. -\subsection{Influence of Capping Agent Coverage on $G$} -To investigate the influence of butanethiol coverage on interfacial -thermal conductance, a series of different coverage Au-butanethiol -surfaces is prepared and solvated with various organic -molecules. These systems are then equilibrated and their interfacial -thermal conductivity are measured with our NIVS algorithm. Table -\ref{tlnUhxnUhxnD} lists these results for direct comparison between -different coverages of butanethiol. To study the isotope effect in -interfacial thermal conductance, deuterated UA-hexane is included as -well. -It turned out that with partial covered butanethiol on the Au(111) -surface, the derivative definition for $G$ (Eq. \ref{derivativeG}) has -difficulty to apply, due to the difficulty in locating the maximum of -change of $\lambda$. Instead, the discrete definition -(Eq. \ref{discreteG}) is easier to apply, as max($\Delta T$) can still -be well-defined. Therefore, $G$'s (not $G^\prime$) are used for this -section. +\section{Discussion} -From Table \ref{tlnUhxnUhxnD}, one can see the significance of the +\subsection{Capping agent acts as a vibrational coupler between solid + and solvent phases} +To investigate the mechanism of interfacial thermal conductance, the +vibrational power spectrum was computed. Power spectra were taken for +individual components in different simulations. To obtain these +spectra, simulations were run after equilibration, in the NVE +ensemble, and without a thermal gradient. Snapshots of configurations +were collected at a frequency that is higher than that of the fastest +vibrations occuring in the simulations. With these configurations, the +velocity auto-correlation functions can be computed: +\begin{equation} +C_A (t) = \langle\vec{v}_A (t)\cdot\vec{v}_A (0)\rangle +\label{vCorr} +\end{equation} +The power spectrum is constructed via a Fourier transform of the +symmetrized velocity autocorrelation function, +\begin{equation} + \hat{f}(\omega) = + \int_{-\infty}^{\infty} C_A (t) e^{-2\pi it\omega}\,dt +\label{fourier} +\end{equation} + +From Figure \ref{coverage}, one can see the significance of the presence of capping agents. Even when a fraction of the Au(111) surface sites are covered with butanethiols, the conductivity would see an enhancement by at least a factor of 3. This indicates the important role cappping agent is playing for thermal transport -phenomena on metal/organic solvent surfaces. +phenomena on metal / organic solvent surfaces. Interestingly, as one could observe from our results, the maximum conductance enhancement (largest $G$) happens while the surfaces are @@ -669,7 +907,8 @@ case, $G$ decrease could not be offset but instead acc would not offset this effect. Eventually, when butanethiol coverage continues to decrease, solvent-capping agent contact actually decreases with the disappearing of butanethiol molecules. In this -case, $G$ decrease could not be offset but instead accelerated. +case, $G$ decrease could not be offset but instead accelerated. [MAY NEED +SNAPSHOT SHOWING THE PHENOMENA / SLAB DENSITY ANALYSIS] A comparison of the results obtained from differenet organic solvents can also provide useful information of the interfacial thermal @@ -679,19 +918,29 @@ difference for the results of $G$. [MAY NEED FIGURE] studies, even though eliminating C-H vibration samplings, still have C-C vibrational frequencies different from each other. However, these differences in the infrared range do not seem to produce an observable -difference for the results of $G$. [MAY NEED FIGURE] +difference for the results of $G$ (Figure \ref{uahxnua}). +\begin{figure} +\includegraphics[width=\linewidth]{uahxnua} +\caption{Vibrational spectra obtained for normal (upper) and + deuterated (lower) hexane in Au-butanethiol/hexane + systems. Butanethiol spectra are shown as reference. Both hexane and + butanethiol were using United-Atom models.} +\label{uahxnua} +\end{figure} + Furthermore, results for rigid body toluene solvent, as well as other UA-hexane solvents, are reasonable within the general experimental -ranges[CITATIONS]. This suggests that explicit hydrogen might not be a -required factor for modeling thermal transport phenomena of systems -such as Au-thiol/organic solvent. +ranges\cite{Wilson:2002uq,cahill:793,PhysRevB.80.195406}. This +suggests that explicit hydrogen might not be a required factor for +modeling thermal transport phenomena of systems such as +Au-thiol/organic solvent. However, results for Au-butanethiol/toluene do not show an identical -trend with those for Au-butanethiol/hexane in that $G$'s remain at +trend with those for Au-butanethiol/hexane in that $G$ remains at approximately the same magnitue when butanethiol coverage differs from 25\% to 75\%. This might be rooted in the molecule shape difference -for plane-like toluene and chain-like {\it n}-hexane. Due to this +for planar toluene and chain-like {\it n}-hexane. Due to this difference, toluene molecules have more difficulty in occupying relatively small gaps among capping agents when their coverage is not too low. Therefore, the solvent-capping agent contact may keep @@ -700,19 +949,7 @@ can see a plateau of $G$ vs. butanethiol coverage in o its effect to the process of interfacial thermal transport. Thus, one can see a plateau of $G$ vs. butanethiol coverage in our results. -[NEED ERROR ESTIMATE] -\begin{figure} -\includegraphics[width=\linewidth]{coverage} -\caption{Comparison of interfacial thermal conductivity ($G$) values - for the Au-butanethiol/solvent interface with various UA models and - different capping agent coverages at $\langle T\rangle\sim$200K - using certain energy flux respectively.} -\label{coverage} -\end{figure} - \subsection{Influence of Chosen Molecule Model on $G$} -[MAY COMBINE W MECHANISM STUDY] - In addition to UA solvent/capping agent models, AA models are included in our simulations as well. Besides simulations of the same (UA or AA) model for solvent and capping agent, different models can be applied @@ -721,7 +958,6 @@ these studies. the previous section. Table \ref{modelTest} summarizes the results of these studies. -[MORE DATA; ERROR ESTIMATE] \begin{table*} \begin{minipage}{\linewidth} \begin{center} @@ -731,35 +967,35 @@ these studies. solvent and capping agent (or without capping agent) at $\langle T\rangle\sim$200K. (D stands for deuterated solvent or capping agent molecules; ``Avg.'' denotes results that are - averages of several simulations.)} + averages of simulations under different $J_z$'s. Error + estimates indicated in parenthesis.)} - \begin{tabular}{ccccc} + \begin{tabular}{llccc} \hline\hline Butanethiol model & Solvent & $J_z$ & $G$ & $G^\prime$ \\ (or bare surface) & model & (GW/m$^2$) & \multicolumn{2}{c}{(MW/m$^2$/K)} \\ \hline - UA & UA hexane & Avg. & 131() & 86.5() \\ - & UA hexane(D) & 1.95 & 153() & 136() \\ - & AA hexane & 1.94 & 135() & 129() \\ - & & 2.86 & 126() & 115() \\ - & UA toluene & 1.96 & 187() & 151() \\ - & AA toluene & 1.89 & 200() & 149() \\ + UA & UA hexane & Avg. & 131(9) & 87(10) \\ + & UA hexane(D) & 1.95 & 153(5) & 136(13) \\ + & AA hexane & Avg. & 131(6) & 122(10) \\ + & UA toluene & 1.96 & 187(16) & 151(11) \\ + & AA toluene & 1.89 & 200(36) & 149(53) \\ \hline - AA & UA hexane & 1.94 & 116() & 129() \\ - & AA hexane & Avg. & 442() & 356() \\ - & AA hexane(D) & 1.93 & 222() & 234() \\ - & UA toluene & 1.98 & 125() & 96.5() \\ - & AA toluene & 3.79 & 487() & 290() \\ + AA & UA hexane & 1.94 & 116(9) & 129(8) \\ + & AA hexane & Avg. & 442(14) & 356(31) \\ + & AA hexane(D) & 1.93 & 222(12) & 234(54) \\ + & UA toluene & 1.98 & 125(25) & 97(60) \\ + & AA toluene & 3.79 & 487(56) & 290(42) \\ \hline - AA(D) & UA hexane & 1.94 & 158() & 172() \\ - & AA hexane & 1.92 & 243() & 191() \\ - & AA toluene & 1.93 & 364() & 322() \\ + AA(D) & UA hexane & 1.94 & 158(25) & 172(4) \\ + & AA hexane & 1.92 & 243(29) & 191(11) \\ + & AA toluene & 1.93 & 364(36) & 322(67) \\ \hline - bare & UA hexane & Avg. & 46.5() & 49.4() \\ - & UA hexane(D) & 0.98 & 43.9() & 43.0() \\ - & AA hexane & 0.96 & 31.0() & 29.4() \\ - & UA toluene & 1.99 & 70.1() & 65.8() \\ + bare & UA hexane & Avg. & 46.5(3.2) & 49.4(4.5) \\ + & UA hexane(D) & 0.98 & 43.9(4.6) & 43.0(2.0) \\ + & AA hexane & 0.96 & 31.0(1.4) & 29.4(1.3) \\ + & UA toluene & 1.99 & 70.1(1.3) & 65.8(0.5) \\ \hline\hline \end{tabular} \label{modelTest} @@ -782,27 +1018,37 @@ the upper bond of experimental value range. This is pr interfaces, using AA model for both butanethiol and hexane yields substantially higher conductivity values than using UA model for at least one component of the solvent and capping agent, which exceeds -the upper bond of experimental value range. This is probably due to -the classically treated C-H vibrations in the AA model, which should -not be appreciably populated at normal temperatures. In comparison, -once either the hexanes or the butanethiols are deuterated, one can -see a significantly lower $G$ and $G^\prime$. In either of these -cases, the C-H(D) vibrational overlap between the solvent and the -capping agent is removed. [MAY NEED FIGURE] Conclusively, the -improperly treated C-H vibration in the AA model produced -over-predicted results accordingly. Compared to the AA model, the UA -model yields more reasonable results with higher computational -efficiency. +the general range of experimental measurement results. This is +probably due to the classically treated C-H vibrations in the AA +model, which should not be appreciably populated at normal +temperatures. In comparison, once either the hexanes or the +butanethiols are deuterated, one can see a significantly lower $G$ and +$G^\prime$. In either of these cases, the C-H(D) vibrational overlap +between the solvent and the capping agent is removed (Figure +\ref{aahxntln}). Conclusively, the improperly treated C-H vibration in +the AA model produced over-predicted results accordingly. Compared to +the AA model, the UA model yields more reasonable results with higher +computational efficiency. +\begin{figure} +\includegraphics[width=\linewidth]{aahxntln} +\caption{Spectra obtained for All-Atom model Au-butanethil/solvent + systems. When butanethiol is deuterated (lower left), its + vibrational overlap with hexane would decrease significantly, + compared with normal butanethiol (upper left). However, this + dramatic change does not apply to toluene as much (right).} +\label{aahxntln} +\end{figure} + However, for Au-butanethiol/toluene interfaces, having the AA butanethiol deuterated did not yield a significant change in the measurement results. Compared to the C-H vibrational overlap between hexane and butanethiol, both of which have alkyl chains, that overlap between toluene and butanethiol is not so significant and thus does -not have as much contribution to the ``Intramolecular Vibration -Redistribution''[CITE HASE]. Conversely, extra degrees of freedom such -as the C-H vibrations could yield higher heat exchange rate between -these two phases and result in a much higher conductivity. +not have as much contribution to the heat exchange +process. Conversely, extra degrees of freedom such as the C-H +vibrations could yield higher heat exchange rate between these two +phases and result in a much higher conductivity. Although the QSC model for Au is known to predict an overly low value for bulk metal gold conductivity\cite{kuang:164101}, our computational @@ -812,45 +1058,42 @@ occupying the interfaces. the accuracy of the interaction descriptions between components occupying the interfaces. -\subsection{Mechanism of Interfacial Thermal Conductance Enhancement - by Capping Agent} -%OR\subsection{Vibrational spectrum study on conductance mechanism} +\subsection{Role of Capping Agent in Interfacial Thermal Conductance} +The vibrational spectra for gold slabs in different environments are +shown as in Figure \ref{specAu}. Regardless of the presence of +solvent, the gold surfaces covered by butanethiol molecules, compared +to bare gold surfaces, exhibit an additional peak observed at the +frequency of $\sim$170cm$^{-1}$, which is attributed to the S-Au +bonding vibration. This vibration enables efficient thermal transport +from surface Au layer to the capping agents. Therefore, in our +simulations, the Au/S interfaces do not appear major heat barriers +compared to the butanethiol / solvent interfaces. -[MAY INTRODUCE PROTOCOL IN METHODOLOGY/COMPUTATIONAL DETAIL, EQN'S] +\subsubsection{Overlap of power spectrum} +Simultaneously, the vibrational overlap between butanethiol and +organic solvents suggests higher thermal exchange efficiency between +these two components. Even exessively high heat transport was observed +when All-Atom models were used and C-H vibrations were treated +classically. Compared to metal and organic liquid phase, the heat +transfer efficiency between butanethiol and organic solvents is closer +to that within bulk liquid phase. -To investigate the mechanism of this interfacial thermal conductance, -the vibrational spectra of various gold systems were obtained and are -shown as in the upper panel of Fig. \ref{vibration}. To obtain these -spectra, one first runs a simulation in the NVE ensemble and collects -snapshots of configurations; these configurations are used to compute -the velocity auto-correlation functions, which is used to construct a -power spectrum via a Fourier transform. +Furthermore, our observation validated previous +results\cite{hase:2010} that the intramolecular heat transport of +alkylthiols is highly effecient. As a combinational effects of these +phenomena, butanethiol acts as a channel to expedite thermal transport +process. The acoustic impedance mismatch between the metal and the +liquid phase can be effectively reduced with the presence of suitable +capping agents. -[MAY RELATE TO HASE'S] - The gold surfaces covered by -butanethiol molecules, compared to bare gold surfaces, exhibit an -additional peak observed at a frequency of $\sim$170cm$^{-1}$, which -is attributed to the vibration of the S-Au bond. This vibration -enables efficient thermal transport from surface Au atoms to the -capping agents. Simultaneously, as shown in the lower panel of -Fig. \ref{vibration}, the large overlap of the vibration spectra of -butanethiol and hexane in the all-atom model, including the C-H -vibration, also suggests high thermal exchange efficiency. The -combination of these two effects produces the drastic interfacial -thermal conductance enhancement in the all-atom model. - -[REDO. MAY NEED TO CONVERT TO JPEG] \begin{figure} \includegraphics[width=\linewidth]{vibration} \caption{Vibrational spectra obtained for gold in different - environments (upper panel) and for Au/thiol/hexane simulation in - all-atom model (lower panel).} -\label{vibration} + environments.} +\label{specAu} \end{figure} -[COMPARISON OF TWO G'S; AU SLAB WIDTHS; ETC] -% The results show that the two definitions used for $G$ yield -% comparable values, though $G^\prime$ tends to be smaller. +[MAY ADD COMPARISON OF AU SLAB WIDTHS BUT NOT MUCH TO TALK ABOUT...] \section{Conclusions} The NIVS algorithm we developed has been applied to simulations of @@ -858,12 +1101,20 @@ conductivities. Our simulations have seen significant effective unphysical thermal flux transferred between the metal and the liquid phase. With the flux applied, we were able to measure the corresponding thermal gradient and to obtain interfacial thermal -conductivities. Our simulations have seen significant conductance -enhancement with the presence of capping agent, compared to the bare -gold/liquid interfaces. The acoustic impedance mismatch between the -metal and the liquid phase is effectively eliminated by proper capping +conductivities. Under steady states, single trajectory simulation +would be enough for accurate measurement. This would be advantageous +compared to transient state simulations, which need multiple +trajectories to produce reliable average results. + +Our simulations have seen significant conductance enhancement with the +presence of capping agent, compared to the bare gold / liquid +interfaces. The acoustic impedance mismatch between the metal and the +liquid phase is effectively eliminated by proper capping agent. Furthermore, the coverage precentage of the capping agent plays -an important role in the interfacial thermal transport process. +an important role in the interfacial thermal transport +process. Moderately lower coverages allow higher contact between +capping agent and solvent, and thus could further enhance the heat +transfer process. Our measurement results, particularly of the UA models, agree with available experimental data. This indicates that our force field @@ -873,22 +1124,28 @@ modelings. vibration would be overly sampled. Compared to the AA models, the UA models have higher computational efficiency with satisfactory accuracy, and thus are preferable in interfacial thermal transport -modelings. +modelings. Of the two definitions for $G$, the discrete form +(Eq. \ref{discreteG}) was easier to use and gives out relatively +consistent results, while the derivative form (Eq. \ref{derivativeG}) +is not as versatile. Although $G^\prime$ gives out comparable results +and follows similar trend with $G$ when measuring close to fully +covered or bare surfaces, the spatial resolution of $T$ profile is +limited for accurate computation of derivatives data. Vlugt {\it et al.} has investigated the surface thiol structures for nanocrystal gold and pointed out that they differs from those of the -Au(111) surface\cite{vlugt:cpc2007154}. This difference might lead to -change of interfacial thermal transport behavior as well. To -investigate this problem, an effective means to introduce thermal flux -and measure the corresponding thermal gradient is desirable for -simulating structures with spherical symmetry. +Au(111) surface\cite{landman:1998,vlugt:cpc2007154}. This difference +might lead to change of interfacial thermal transport behavior as +well. To investigate this problem, an effective means to introduce +thermal flux and measure the corresponding thermal gradient is +desirable for simulating structures with spherical symmetry. - \section{Acknowledgments} Support for this project was provided by the National Science Foundation under grant CHE-0848243. Computational time was provided by the Center for Research Computing (CRC) at the University of Notre -Dame. \newpage +Dame. +\newpage \bibliography{interfacial}