--- trunk/COonPt/firstTry.tex 2012/12/20 21:36:33 3839 +++ trunk/COonPt/firstTry.tex 2013/03/15 12:51:01 3876 @@ -1,4 +1,13 @@ -\documentclass[11pt]{article} +\documentclass[journal = jpccck, manuscript = article]{achemso} +\setkeys{acs}{usetitle = true} +\usepackage{achemso} +\usepackage{caption} +\usepackage{float} +\usepackage{geometry} +\usepackage{natbib} +\usepackage{setspace} +\usepackage{xkeyval} +%%%%%%%%%%%%%%%%%%%%%%% \usepackage{amsmath} \usepackage{amssymb} \usepackage{times} @@ -6,13 +15,14 @@ \usepackage{setspace} \usepackage{endfloat} \usepackage{caption} -%\usepackage{tabularx} +\usepackage{tabularx} +\usepackage{longtable} \usepackage{graphicx} \usepackage{multirow} -%\usepackage{booktabs} -%\usepackage{bibentry} -%\usepackage{mathrsfs} -\usepackage[square, comma, sort&compress]{natbib} +\usepackage{multicol} + +\usepackage[version=3]{mhchem} % this is a great package for formatting chemical reactions +% \usepackage[square, comma, sort&compress]{natbib} \usepackage{url} \pagestyle{plain} \pagenumbering{arabic} \oddsidemargin 0.0cm \evensidemargin 0.0cm \topmargin -21pt \headsep 10pt \textheight @@ -22,13 +32,27 @@ %\AtBeginDelayedFloats{\renewcomand{\baselinestretch}{1.66}} \setlength{\abovecaptionskip}{20 pt} \setlength{\belowcaptionskip}{30 pt} +% \bibpunct{}{}{,}{s}{}{;} -\bibpunct{}{}{,}{s}{}{;} -\bibliographystyle{achemso} +%\citestyle{nature} +% \bibliographystyle{achemso} -\begin{document} +\title{Molecular Dynamics simulations of the surface reconstructions + of Pt(557) and Au(557) under exposure to CO} +\author{Joseph R. Michalka} +\author{Patrick W. McIntyre} +\author{J. Daniel Gezelter} +\email{gezelter@nd.edu} +\affiliation[University of Notre Dame]{251 Nieuwland Science Hall\\ + Department of Chemistry and Biochemistry\\ University of Notre + Dame\\ Notre Dame, Indiana 46556} +\keywords{} + +\begin{document} + + %% %Introduction % Experimental observations @@ -47,27 +71,20 @@ %Summary %% -%Title -\title{Molecular Dynamics simulations of the surface reconstructions - of Pt(557) and Au(557) under exposure to CO} -\author{Joseph R. Michalka, Patrick W. McIntyre and J. Daniel -Gezelter\footnote{Corresponding author. \ Electronic mail: gezelter@nd.edu} \\ -Department of Chemistry and Biochemistry,\\ -University of Notre Dame\\ -Notre Dame, Indiana 46556} - -%Date -\date{Dec 15, 2012} - -%authors - -% make the title -\maketitle - -\begin{doublespace} - \begin{abstract} +We examine surface reconstructions of Pt and Au(557) under +various CO coverages using molecular dynamics in order to +explore possible mechanisms for any observed reconstructions +and their dynamics. The metal-CO interactions were parameterized +as part of this work so that an efficient large-scale treatment of +this system could be undertaken. The large difference in binding +strengths of the metal-CO interactions was found to play a significant +role with regards to step-edge stability and adatom diffusion. A +small correlation between coverage and the diffusion constant +was also determined. The energetics of CO adsorbed to the surface +is sufficient to explain the reconstructions observed on the Pt +systems and the lack of reconstruction of the Au systems. \end{abstract} @@ -100,24 +117,35 @@ This work an effort to understand the mechanism and ti reversible restructuring under exposure to moderate pressures of carbon monoxide.\cite{Tao:2010} -This work an effort to understand the mechanism and timescale for +This work is an investigation into the mechanism and timescale for surface restructuring using molecular simulations. Since the dynamics -of the process is of particular interest, we utilize classical force +of the process are of particular interest, we employ classical force fields that represent a compromise between chemical accuracy and the -computational efficiency necessary to observe the process of interest. +computational efficiency necessary to simulate the process of interest. +Since restructuring typically occurs as a result of specific interactions of the +catalyst with adsorbates, in this work, two metal systems exposed +to carbon monoxide were examined. The Pt(557) surface has already been shown +to undergo a large scale reconstruction under certain conditions.\cite{Tao:2010} +The Au(557) surface, because of a weaker interaction with CO, is seen as less +likely to undergo this kind of reconstruction. However, Peters et al.\cite{Peters:2000} +and Piccolo et al.\cite{Piccolo:2004} have both observed CO-induced +reconstruction of a Au(111) surface. Peters et al. saw a relaxation to the +22 x $\sqrt{3}$ cell. They argued that only a few Au atoms +become adatoms, limiting the stress of this reconstruction while +allowing the rest to relax and approach the ideal (111) +configuration. They did not see the usual herringbone pattern being greatly +affected by this relaxation. Piccolo et al. on the other hand, did see a +disruption of the herringbone pattern as CO was adsorbed to the +surface. Both groups suggested that the preference CO shows for +low-coordinated Au atoms was the primary driving force for the reconstruction. -Since restructuring occurs as a result of specific interactions of the -catalyst with adsorbates, two metal systems exposed to carbon monoxide -were examined in this work. The Pt(557) surface has already been shown -to reconstruct under certain conditions. The Au(557) surface, because -of a weaker interaction with CO, is less likely to undergo this kind -of reconstruction. MORE HERE ON PT AND AU PREVIOUS WORK. + %Platinum molecular dynamics %gold molecular dynamics \section{Simulation Methods} -The challenge in modeling any solid/gas interface problem is the +The challenge in modeling any solid/gas interface is the development of a sufficiently general yet computationally tractable model of the chemical interactions between the surface atoms and adsorbates. Since the interfaces involved are quite large (10$^3$ - @@ -133,7 +161,7 @@ Au-Au and Pt-Pt interactions, while modeling the CO us Coulomb potential. For this work, we have used classical molecular dynamics with potential energy surfaces that are specifically tuned for transition metals. In particular, we used the EAM potential for -Au-Au and Pt-Pt interactions, while modeling the CO using a rigid +Au-Au and Pt-Pt interactions\cite{EAM}. The CO was modeled using a rigid three-site model developed by Straub and Karplus for studying photodissociation of CO from myoglobin.\cite{Straub} The Au-CO and Pt-CO cross interactions were parameterized as part of this work. @@ -146,7 +174,7 @@ parameter sets. The glue model of Ercolessi {\it et al methods,\cite{Daw84,Foiles86,Johnson89,Daw89,Plimpton93,Voter95a,Lu97,Alemany98} but other models like the Finnis-Sinclair\cite{Finnis84,Chen90} and the quantum-corrected Sutton-Chen method\cite{QSC,Qi99} have simpler -parameter sets. The glue model of Ercolessi {\it et al.} is among the +parameter sets. The glue model of Ercolessi et al. is among the fastest of these density functional approaches.\cite{Ercolessi88} In all of these models, atoms are conceptualized as a positively charged core with a radially-decaying valence electron distribution. To @@ -164,8 +192,8 @@ $\phi_{ij}(r_{ij})$ is an pairwise term that is meant V_i = F[ \bar{\rho}_i ] + \sum_{j \neq i} \phi_{ij}(r_{ij}) \end{equation*} where $F[ \bar{\rho}_i ]$ is an energy embedding functional, and -$\phi_{ij}(r_{ij})$ is an pairwise term that is meant to represent the -overlap of the two positively charged cores. +$\phi_{ij}(r_{ij})$ is a pairwise term that is meant to represent the +repulsive overlap of the two positively charged cores. % The {\it modified} embedded atom method (MEAM) adds angular terms to % the electron density functions and an angular screening factor to the @@ -176,28 +204,38 @@ The EAM, Finnis-Sinclair, and the Quantum Sutton-Chen % metals,\cite{Lee:2001qf} and also interfaces.\cite{Beurden:2002ys}) % MEAM presents significant additional computational costs, however. -The EAM, Finnis-Sinclair, and the Quantum Sutton-Chen potentials +The EAM, Finnis-Sinclair, and the Quantum Sutton-Chen (QSC) potentials have all been widely used by the materials simulation community for simulations of bulk and nanoparticle properties,\cite{Chui:2003fk,Wang:2005qy,Medasani:2007uq} melting,\cite{Belonoshko00,sankaranarayanan:155441,Sankaranarayanan:2005lr} fracture,\cite{Shastry:1996qg,Shastry:1998dx} crack propagation,\cite{BECQUART:1993rg} and alloying -dynamics.\cite{Shibata:2002hh} All of these potentials have their -strengths and weaknesses. One of the strengths common to all of the -methods is the relatively large library of metals for which these -potentials have been -parameterized.\cite{Foiles86,PhysRevB.37.3924,Rifkin1992,mishin99:_inter,mishin01:cu,mishin02:b2nial,zope03:tial_ap,mishin05:phase_fe_ni} +dynamics.\cite{Shibata:2002hh} One of EAM's strengths +is its sensitivity to small changes in structure. This arises +from the original parameterization, where the interactions +up to the third nearest neighbor were taken into account.\cite{Voter95a} +Comparing that to the glue model of Ercolessi et al.\cite{Ercolessi88} +which is only parameterized up to the nearest-neighbor +interactions, EAM is a suitable choice for systems where +the bulk properties are of secondary importance to low-index +surface structures. Additionally, the similarity of EAMs functional +treatment of the embedding energy to standard density functional +theory (DFT) makes fitting DFT-derived cross potentials with adsorbates somewhat easier. +\cite{Foiles86,PhysRevB.37.3924,Rifkin1992,mishin99:_inter,mishin01:cu,mishin02:b2nial,zope03:tial_ap,mishin05:phase_fe_ni} + + + \subsection{Carbon Monoxide model} -Since previous explanations for the surface rearrangements center on -the large linear quadrupole moment of carbon monoxide, the model -chosen for this molecule exhibits this property in an efficient -manner. We used a model first proposed by Karplus and Straub to study -the photodissociation of CO from myoglobin.\cite{Straub} The Straub and -Karplus model is a rigid three site model which places a massless M -site at the center of mass along the CO bond. The geometry used along -with the interaction parameters are reproduced in Table~1. The effective +Previous explanations for the surface rearrangements center on +the large linear quadrupole moment of carbon monoxide.\cite{Tao:2010} +We used a model first proposed by Karplus and Straub to study +the photodissociation of CO from myoglobin because it reproduces +the quadrupole moment well.\cite{Straub} The Straub and +Karplus model treats CO as a rigid three site molecule with a massless M +site at the molecular center of mass. The geometry and interaction +parameters are reproduced in Table~\ref{tab:CO}. The effective dipole moment, calculated from the assigned charges, is still small (0.35 D) while the linear quadrupole (-2.40 D~\AA) is close to the experimental (-2.63 D~\AA)\cite{QuadrupoleCO} and quantum @@ -206,37 +244,40 @@ mechanical predictions (-2.46 D~\AA)\cite{QuadrupoleCO \begin{table}[H] \caption{Positions, Lennard-Jones parameters ($\sigma$ and $\epsilon$), and charges for the CO-CO - interactions borrowed from Ref. \bibpunct{}{}{,}{n}{}{,} \protect\cite{Straub}. Distances are in \AA~, energies are + interactions in Ref.\bibpunct{}{}{,}{n}{}{,} \protect\cite{Straub}. Distances are in \AA, energies are in kcal/mol, and charges are in atomic units.} \centering \begin{tabular}{| c | c | ccc |} \hline & {\it z} & $\sigma$ & $\epsilon$ & q\\ \hline -\textbf{C} & -0.6457 & 0.0262 & 3.83 & -0.75 \\ -\textbf{O} & 0.4843 & 0.1591 & 3.12 & -0.85 \\ +\textbf{C} & -0.6457 & 3.83 & 0.0262 & -0.75 \\ +\textbf{O} & 0.4843 & 3.12 & 0.1591 & -0.85 \\ \textbf{M} & 0.0 & - & - & 1.6 \\ \hline \end{tabular} +\label{tab:CO} \end{table} \subsection{Cross-Interactions between the metals and carbon monoxide} -Since the adsorption of CO onto a platinum surface has been the focus +Since the adsorption of CO onto a Pt surface has been the focus of much experimental \cite{Yeo, Hopster:1978, Ertl:1977, Kelemen:1979} and theoretical work \cite{Beurden:2002ys,Pons:1986,Deshlahra:2009,Feibelman:2001,Mason:2004} there is a significant amount of data on adsorption energies for CO on -clean metal surfaces. Parameters reported by Korzeniewski {\it et - al.}\cite{Pons:1986} were a starting point for our fits, which were +clean metal surfaces. An earlier model by Korzeniewski {\it et + al.}\cite{Pons:1986} served as a starting point for our fits. The parameters were modified to ensure that the Pt-CO interaction favored the atop binding -position on Pt(111). This resulting binding energies are on the higher -side of the experimentally-reported values. Following Korzeniewski -{\it et al.},\cite{Pons:1986} the Pt-C interaction was fit to a deep +position on Pt(111). These parameters are reproduced in Table~\ref{tab:co_parameters}. +The modified parameters yield binding energies that are slightly higher +than the experimentally-reported values as shown in Table~\ref{tab:co_energies}. Following Korzeniewski +et al.,\cite{Pons:1986} the Pt-C interaction was fit to a deep Lennard-Jones interaction to mimic strong, but short-ranged partial binding between the Pt $d$ orbitals and the $\pi^*$ orbital on CO. The -Pt-O interaction was parameterized to a Morse potential with a large -range parameter ($r_o$). In most cases, this contributes a weak +Pt-O interaction was modeled with a Morse potential with a large +equilibrium distance, ($r_o$). These choices ensure that the C is preferred +over O as the surface-binding atom. In most cases, the Pt-O parameterization contributes a weak repulsion which favors the atop site. The resulting potential-energy surface suitably recovers the calculated Pt-C separation length (1.6~\AA)\cite{Beurden:2002ys} and affinity for the atop binding @@ -245,45 +286,45 @@ The Au-C and Au-O cross-interactions were fit using Le %where did you actually get the functionals for citation? %scf calculations, so initial relaxation was of the four layers, but two layers weren't kept fixed, I don't think %same cutoff for slab and slab + CO ? seems low, although feibelmen had values around there... -The Au-C and Au-O cross-interactions were fit using Lennard-Jones and +The Au-C and Au-O cross-interactions were also fit using Lennard-Jones and Morse potentials, respectively, to reproduce Au-CO binding energies. - -The fits were refined against gas-surface DFT calculations with a +The limited experimental data for CO adsorption on Au required refining the fits against plane-wave DFT calculations. +Adsorption energies were obtained from gas-surface DFT calculations with a periodic supercell plane-wave basis approach, as implemented in the -{\sc Quantum ESPRESSO} package.\cite{QE-2009} Electron cores are +{\sc Quantum ESPRESSO} package.\cite{QE-2009} Electron cores were described with the projector augmented-wave (PAW) method,\cite{PhysRevB.50.17953,PhysRevB.59.1758} with plane waves included to an energy cutoff of 20 Ry. Electronic energies are computed with the PBE implementation of the generalized gradient approximation (GGA) for gold, carbon, and oxygen that was constructed by Rappe, Rabe, Kaxiras, and Joannopoulos.\cite{Perdew_GGA,RRKJ_PP} -Ionic relaxations were performed until the energy difference between -subsequent steps was less than $10^{-8}$ Ry. In testing the CO-Au -interaction, Au(111) supercells were constructed of four layers of 4 +In testing the Au-CO interaction, Au(111) supercells were constructed of four layers of 4 Au x 2 Au surface planes and separated from vertical images by six -layers of vacuum space. The surface atoms were all allowed to relax. -Supercell calculations were performed nonspin-polarized with a 4 x 4 x -4 Monkhorst-Pack {\bf k}-point sampling of the first Brillouin -zone.\cite{Monkhorst:1976,PhysRevB.13.5188} The relaxed gold slab was +layers of vacuum space. The surface atoms were all allowed to relax +before CO was added to the system. Electronic relaxations were +performed until the energy difference between subsequent steps +was less than $10^{-8}$ Ry. Nonspin-polarized supercell calculations +were performed with a 4~x~4~x~4 Monkhorst-Pack {\bf k}-point sampling of the first Brillouin +zone.\cite{Monkhorst:1976} The relaxed gold slab was then used in numerous single point calculations with CO at various heights (and angles relative to the surface) to allow fitting of the empirical force field. %Hint at future work -The parameters employed in this work are shown in Table 2 and the -binding energies on the 111 surfaces are displayed in Table 3. To -speed up the computations, charge transfer and polarization are not -being treated in this model, although these effects are likely to -affect binding energies and binding site -preferences.\cite{Deshlahra:2012} +The parameters employed for the metal-CO cross-interactions in this work +are shown in Table~\ref{tab:co_parameters} and the binding energies on the +(111) surfaces are displayed in Table~\ref{tab:co_energies}. Charge transfer +and polarization are neglected in this model, although these effects are likely to +affect binding energies and binding site preferences, and will be addressed in +future work. %Table of Parameters %Pt Parameter Set 9 %Au Parameter Set 35 \begin{table}[H] - \caption{Best fit parameters for metal-CO cross-interactions. Metal-C - interactions are modeled with Lennard-Jones potential, while the - (mostly-repulsive) metal-O interactions were fit to Morse + \caption{Best fit parameters for metal-CO cross-interactions. Metal-C + interactions are modeled with Lennard-Jones potentials. While the + metal-O interactions were fit to Morse potentials. Distances are given in \AA~and energies in kcal/mol. } \centering \begin{tabular}{| c | cc | c | ccc |} @@ -295,12 +336,13 @@ preferences.\cite{Deshlahra:2012} \hline \end{tabular} +\label{tab:co_parameters} \end{table} %Table of energies \begin{table}[H] - \caption{Adsorption energies for CO on M(111) using the potentials - described in this work. All values are in eV} + \caption{Adsorption energies for a single CO at the atop site on M(111) at the atop site using the potentials + described in this work. All values are in eV.} \centering \begin{tabular}{| c | cc |} \hline @@ -309,104 +351,426 @@ preferences.\cite{Deshlahra:2012} \multirow{2}{*}{\textbf{Pt-CO}} & \multirow{2}{*}{-1.9} & -1.4 \bibpunct{}{}{,}{n}{}{,} (Ref. \protect\cite{Kelemen:1979}) \\ & & -1.9 \bibpunct{}{}{,}{n}{}{,} (Ref. \protect\cite{Yeo}) \\ \hline - \textbf{Au-CO} & -0.39 & -0.40 \bibpunct{}{}{,}{n}{}{,} (Ref. \protect\cite{TPD_Gold}) \\ + \textbf{Au-CO} & -0.39 & -0.40 \bibpunct{}{}{,}{n}{}{,} (Ref. \protect\cite{TPDGold}) \\ \hline \end{tabular} +\label{tab:co_energies} \end{table} \subsection{Pt(557) and Au(557) metal interfaces} - -Our model systems are composed of 3888 Pt atoms and 3384 Au atoms in a -FCC crystal that have been cut along the 557 plane so that they are -periodic in the {\it x} and {\it y} directions, and have been rotated -to expose two parallel 557 cuts along the positive and negative {\it - z}-axis. Simulations of the bare metal interfaces at temperatures -ranging from 300~K to 1200~K were done to observe the relative +Our Pt system is an orthorhombic periodic box of dimensions +54.482~x~50.046~x~120.88~\AA~while our Au system has +dimensions of 57.4~x~51.9285~x~100~\AA. +The systems are arranged in a FCC crystal that have been cut +along the (557) plane so that they are periodic in the {\it x} and +{\it y} directions, and have been oriented to expose two aligned +(557) cuts along the extended {\it z}-axis. Simulations of the +bare metal interfaces at temperatures ranging from 300~K to +1200~K were performed to confirm the relative stability of the surfaces without a CO overlayer. -The different bulk (and surface) melting temperatures (1337~K for Au -and 2045~K for Pt) suggest that the reconstruction may happen at -different temperatures for the two metals. To copy experimental -conditions for the CO-exposed surfaces, the bare surfaces were +The different bulk melting temperatures (1345~$\pm$~10~K for Au\cite{Au:melting} +and $\sim$~2045~K for Pt\cite{Pt:melting}) suggest that any possible reconstruction should happen at +different temperatures for the two metals. The bare Au and Pt surfaces were initially run in the canonical (NVT) ensemble at 800~K and 1000~K -respectively for 100 ps. Each surface was exposed to a range of CO +respectively for 100 ps. The two surfaces were relatively stable at these +temperatures when no CO was present, but experienced increased surface +mobility on addition of CO. Each surface was then dosed with different concentrations of CO that was initially placed in the vacuum region. Upon full adsorption, -these amounts correspond to 0\%, 5\%, 25\%, 33\%, and 50\% surface -coverage. Because of the difference in binding energies, the platinum -systems very rarely had CO that was not bound to the surface, while -the gold surfaces often had a significant CO population in the gas +these concentrations correspond to 0\%, 5\%, 25\%, 33\%, and 50\% surface +coverage. Higher coverages resulted in the formation of a double layer of CO, +which introduces artifacts that are not relevant to (557) reconstruction. +Because of the difference in binding energies, nearly all of the CO was bound to the Pt surface, while +the Au surfaces often had a significant CO population in the gas phase. These systems were allowed to reach thermal equilibrium (over -5 ns) before being shifted to the microcanonical (NVE) ensemble for -data collection. All of the systems examined had at least 40 ns in the -data collection stage, although simulation times for some of the -systems exceeded 200ns. All simulations were run using the open -source molecular dynamics package, OpenMD.\cite{Ewald,OOPSE,OpenMD} +5~ns) before being run in the microcanonical (NVE) ensemble for +data collection. All of the systems examined had at least 40~ns in the +data collection stage, although simulation times for some Pt of the +systems exceeded 200~ns. Simulations were carried out using the open +source molecular dynamics package, OpenMD.\cite{Ewald,OOPSE} -% Just results, leave discussion for discussion section + + + +% RESULTS +% \section{Results} -Tao {\it et al.} showed experimentally that the Pt(557) surface -undergoes two separate reconstructions upon CO -adsorption.\cite{Tao:2010} The first reconstruction involves a -doubling of the step edge height which is accomplished by a doubling -of the plateau length. The second reconstruction led to the formation -of triangular clusters that arrange themselves along the lengthened -plateaus. +\subsection{Structural remodeling} +The surfaces of both systems, upon dosage of CO, began +to undergo extensive remodeling that was not observed in the bare +systems. The bare metal surfaces +experienced minor roughening of the step-edge because +of the elevated temperatures, but the +(557) lattice was well-maintained throughout the simulation +time. The Au systems were limited to greater amounts of +roughening, i.e. breakup of the step-edge, and some step +wandering. The lower coverage Pt systems experienced +similar restructuring but to a greater extent when +compared to the Au systems. The 50\% coverage +Pt system was unique among our simulations in that it +formed numerous double layers through step coalescence, +similar to results reported by Tao et al.\cite{Tao:2010} -The primary observation and results of our simulation is that the -presence of CO overlayer on Pt(557) causes the same kind of -reconstruction observed experimentally. The 6-atom 111 facets -initially become disordered, and after 20-40 ns, a double-layer (with -a 2-atom step between terraces) forms. However, we did not observe -the triangular cluster formation that was observed at longer times in -the experiments. Without the CO present on the Pt(557) surface, there -was some disorder at the step edges, but no significant restructuring -was observed. -In these simulations, the Au(557) surface did not exhibit any -significant restructuring either with or without the presence of a CO -overlayer. +\subsubsection{Step wandering} +The 0\% coverage surfaces for both metals showed minimal +movement at their respective run temperatures. As the CO +coverage increased however, the mobility of the surface, +described through adatom diffusion and step-edge wandering, +also increased. Except for the 50\% Pt system, the step-edges +did not coalesce in any of the other simulations, instead +preferring to keep nearly the same distance between steps +as in the original (557) lattice, $\sim$13\AA for Pt and $\sim$14\AA for Au. +Previous work by Williams et al.\cite{Williams:1991, Williams:1994} +highlights the repulsion that exists between step-edges even +when no direct interactions are present in the system. This +repulsion arises because step-edge crossing is not allowed +which constrains the entropy. This entropic repulsion does +not completely define the interactions between steps, which +is why some surfaces will undergo step coalescence, where +additional attractive interactions can overcome the repulsion.\cite{Williams:1991} +The presence and concentration of adsorbates, as shown in +this work, can affect these step interactions, potentially leading +to a new surface structure as the thermodynamic minimum. -\subsection{Transport of surface metal atoms} -An ideal metal surface displaying a low energy (111) face is unlikely -to experience much surface diffusion because of the large vacancy -formation energy for atoms at the surface. This implies that -significant energy must be expended to lift an atom out of the flat -face so it can migrate on the surface. Rougher surfaces and those -that already contain numerous adatoms, step edges, and kinks, are -expected to have higher surface diffusion rates. Metal atoms that are -mobile on the surface were observed to leave and then rejoin step -edges or other formations. They may travel together or as isolated -atoms. The primary challenge of quantifying the overall surface -mobility is in defining ``mobile'' vs. ``static'' atoms. +\subsubsection{Double layers} +Tao et al.\cite{Tao:2010} have shown experimentally that the Pt(557) surface +undergoes two separate reconstructions upon CO adsorption.\cite{Tao:2010} +The first involves a doubling of the step height and plateau length. +Similar behavior has been seen on numerous surfaces +at varying conditions: Ni(977), Si(111).\cite{Williams:1994,Williams:1991,Pearl} +Of the two systems we examined, the Pt system showed a greater +propensity for reconstruction when compared to the Au system +because of the larger surface mobility and extent of step wandering. +The amount of reconstruction is strongly correlated to the amount of CO +adsorbed upon the surface. This appears to be related to the +effect that adsorbate coverage has on edge breakup and on the +surface diffusion of metal adatoms. While both systems displayed +step-edge wandering, only the 50\% Pt surface underwent the +doubling seen by Tao et al.\cite{Tao:2010} within the time scales studied here. +Over longer periods, (150~ns) two more double layers formed +on this interface. Although double layer formation did not occur +in the other Pt systems, they show more step-wandering and +general roughening compared to their Au counterparts. The +50\% Pt system is highlighted in Figure \ref{fig:reconstruct} at +various times along the simulation showing the evolution of a double layer step-edge. -A particle was considered mobile once it had traveled more than 2~\AA~ -between saved configurations (10-100 ps). Restricting the transport -calculations to only mobile atoms eliminates all of the bulk metal as -well as any surface atoms that remain fixed for a significant length -of time. Since diffusion on a surface is strongly affected by local -structures, the diffusion parallel to the step edges was determined -separately from the diffusion perpendicular to these edges. The -parallel and perpendicular diffusion constants (determined using -linear fits to the mean squared displacement) are shown in figure \ref{fig:diff}. +The second reconstruction on the Pt(557) surface observed by +Tao involved the formation of triangular clusters that stretched +across the plateau between two step-edges. Neither system, within +the 40~ns time scale or the extended simulation time of 150~ns for +the 50\% Pt system, experienced this reconstruction. -%While an ideal metallic surface is unlikely to experience much surface diffusion, high-index surfaces have large numbers of low-coordinated atoms which have a much easier time overcoming the energetic barriers limiting diffusion, leading to easier surface reconstructions. Surface movement was divided between the parallel ($\parallel$) and perpendicular ($\perp$) directions relative to the step edge. We were then able to calculate diffusion constants as a function of CO coverage. As can be seen in Table 4, the presence and amount of CO directly affects the diffusion constants of surface platinum atoms. The presence of two 50\% coverage systems is to show how the diffusion process is affected by time. The majority of the systems were run for approximately 50 ns while the half monolayer system has been running continuously. The lowered diffusion constant at longer run times will be examined in-depth in the discussion section. +%Evolution of surface +\begin{figure}[H] +\includegraphics[width=\linewidth]{ProgressionOfDoubleLayerFormation_yellowCircle.png} +\caption{The Pt(557) / 50\% CO system at a sequence of times after + initial exposure to the CO: (a) 258~ps, (b) 19~ns, (c) 31.2~ns, and + (d) 86.1~ns. Disruption of the (557) step-edges occurs quickly. The + doubling of the layers appears only after two adjacent step-edges + touch. The circled spot in (b) nucleated the growth of the double + step observed in the later configurations.} + \label{fig:reconstruct} +\end{figure} +\subsection{Dynamics} +Previous atomistic simulations of stepped surfaces dealt largely +with the energetics and structures at different conditions +\cite{Williams:1991,Williams:1994}. Consequently, the most common +technique utilized to date has been Monte Carlo sampling. Monte Carlo approaches give an efficient +sampling of the equilibrium thermodynamic landscape at the expense +of ignoring the dynamics of the system. Previous experimental work by Pearl and +Sibener\cite{Pearl}, using STM, has been able to capture the coalescing +of steps on Ni(977). The time scale of the image acquisition, +$\sim$70~s/image provides an upper bound for the time required for +the doubling to occur. By utilizing Molecular Dynamics we were able to probe the dynamics of these reconstructions and in this section we give data on dynamic and +transport properties, e.g. diffusion, layer formation time, etc. + + +\subsubsection{Transport of surface metal atoms} +%forcedSystems/stepSeparation +The movement or wandering of a step-edge is a cooperative effect +arising from the individual movements of the atoms making up the steps. An ideal metal surface +displaying a low index facet, (111) or (100), is unlikely to experience +much surface diffusion because of the large energetic barrier that must +be overcome to lift an atom out of the surface. The presence of step-edges and other surface features +on higher-index facets provides a lower energy source for mobile metal atoms. +Breaking away from the step-edge on a clean surface still imposes an +energetic penalty around $\sim$~45 kcal/mol, but this is easier than lifting +the same metal atom vertically out of the surface, \textgreater~60 kcal/mol. +The penalty lowers significantly when CO is present in sufficient quantities +on the surface. For certain distributions of CO, see Figures \ref{fig:sketchGraphic} and \ref{fig:sketchEnergies}, the penalty can fall to as low as +$\sim$~20 kcal/mol. Once an adatom exists on the surface, the barrier for +diffusion is negligible ( \textless~4 kcal/mol for a Pt adatom). These adatoms are then +able to explore the terrace before rejoining either their original step-edge or +becoming a part of a different edge. It is a difficult process for an atom +to traverse to a separate terrace although the presence of CO can lower the +energy barrier required to lift or lower an adatom. By tracking the mobility of individual +metal atoms on the Pt and Au surfaces we were able to determine the relative +diffusion constants, as well as how varying coverages of CO affect the diffusion. Close +observation of the mobile metal atoms showed that they were typically in +equilibrium with the step-edges, dynamically breaking apart and rejoining the edges. +At times, their motion was concerted and two or more adatoms would be +observed moving together across the surfaces. + +A particle was considered ``mobile'' once it had traveled more than 2~\AA~ +between saved configurations of the system (typically 10-100 ps). An atom that was +truly mobile would typically travel much greater distances than this, but the 2~\AA~cutoff +was used to prevent swamping the diffusion data with the in-place vibrational +movement of buried atoms. Diffusion on a surface is strongly affected by +local structures and in this work, the presence of single and double layer +step-edges causes the diffusion parallel to the step-edges to be larger than +the diffusion perpendicular to these edges. Parallel and perpendicular +diffusion constants are shown in Figure \ref{fig:diff}. + +%Diffusion graph \begin{figure}[H] -\includegraphics[width=\linewidth]{DiffusionComparison_errorXY_remade.pdf} +\includegraphics[width=\linewidth]{DiffusionComparison_errorXY_remade_20ns.pdf} \caption{Diffusion constants for mobile surface atoms along directions parallel ($\mathbf{D}_{\parallel}$) and perpendicular - ($\mathbf{D}_{\perp}$) to the 557 step edges as a function of CO - surface coverage. Diffusion parallel to the step edge is higher + ($\mathbf{D}_{\perp}$) to the (557) step-edges as a function of CO + surface coverage. Diffusion parallel to the step-edge is higher than that perpendicular to the edge because of the lower energy - barrier associated with going from approximately 7 nearest neighbors - to 5, as compared to the 3 of an adatom. Additionally, the observed - maximum and subsequent decrease for the Pt system suggests that the - CO self-interactions are playing a significant role with regards to - movement of the platinum atoms around and more importantly across - the surface. } + barrier associated with traversing along the edge as compared to + completely breaking away. The two reported diffusion constants for + the 50\% Pt system arise from different sample sets. The lower values + correspond to the same 40~ns amount that all of the other systems were + examined at, while the larger values correspond to a 20~ns period } \label{fig:diff} \end{figure} +The lack of a definite trend in the Au diffusion data in Figure \ref{fig:diff} is likely due +to the weaker bonding between Au and CO. This leads to a lower observed +coverage ({\it x}-axis) when compared to dosage amount, which +then further limits the effect the CO can have on surface diffusion. The correlation +between coverage and Pt diffusion rates conversely shows a +definite trend marred by the highest coverage surface. Two +explanations arise for this drop. First, upon a visual inspection of +the system, after a double layer has been formed, it maintains its +stability strongly and is no longer a good source for adatoms and so +atoms that had been tracked for mobility data have now been buried. By +performing the same diffusion calculation but on a shorter run time +(20~ns), only including data before the formation of the double layer, we obtain +the larger values for both $\mathbf{D}_{\parallel}$ and $\mathbf{D}_{\perp}$ at the 50\% coverage. +This places the parallel diffusion constant more closely in line with the +expected trend, while the perpendicular diffusion constant does not +drop as far. A secondary explanation arising from our analysis of the +mechanism of double layer formation focuses on the effect that CO on the +surface has with respect to overcoming surface diffusion of Pt. If the +coverage is too sparse, the Pt engages in minimal interactions and +thus minimal diffusion. As coverage increases, there are more favorable +arrangements of CO on the surface allowing the formation of a path, +a minimum energy trajectory, for the adatom to explore the surface. +As the CO is constantly moving on the surface, this path is constantly +changing. If the coverage becomes too great, the paths could +potentially be clogged leading to a decrease in diffusion despite +their being more adatoms and step-wandering. + + + +\subsubsection{Dynamics of double layer formation} +The increased diffusion on Pt at the higher +CO coverages plays a primary role in double layer formation. However, this is not +a complete explanation -- the 33\%~Pt system +has higher diffusion constants but did not show +any signs of edge doubling in the observed run time. On the +50\%~Pt system, one layer formed within the first 40~ns of simulation time, while two more were formed as the system was run for an additional +110~ns (150~ns total). Previous experimental +work gives insight into the upper bounds of the +time required for step coalescence.\cite{Williams:1991,Pearl} +In this system, as seen in Figure \ref{fig:reconstruct}, the first +appearance of a double layer, appears at 19~ns +into the simulation. Within 12~ns of this nucleation event, nearly half of the step has +formed the double layer and by 86~ns, the complete layer +has been flattened out. The double layer could be considered +``complete" by 37~ns but remains a bit rough. From the +appearance of the first nucleation event to the first observed double layer, the process took $\sim$20~ns. Another +$\sim$40~ns was necessary for the layer to completely straighten. +The other two layers in this simulation formed over periods of +22~ns and 42~ns respectively. Comparing this to the upper +bounds of the image scan, it is likely that most aspects of this +reconstruction occur very rapidly. A possible explanation +for this rapid reconstruction is the elevated temperatures +under which our systems were simulated. It is probable that the process would +take longer at lower temperatures. + + + + + + +%Sketch graphic of different configurations +\begin{figure}[H] +\includegraphics[width=0.8\linewidth, height=0.8\textheight]{COpathsSketch.pdf} +\caption{The dark grey atoms refer to the upper ledge, while the white atoms are +the lower terrace. The blue highlighted atoms had a CO in a vertical atop position +upon them. These are a sampling of the configurations examined to gain a more +complete understanding of the effects CO has on surface diffusion and edge breakup. +Energies associated with each configuration are displayed in Figure \ref{fig:SketchEnergies}.} +\label{fig:SketchGraphic} +\end{figure} + +%energy graph corresponding to sketch graphic +\begin{figure}[H] +\includegraphics[width=\linewidth]{stepSeparationComparison.pdf} +\caption{The energy curves directly correspond to the labeled model +surface in Figure \ref{fig:SketchGraphic}. All energy curves are relative +to their initial configuration so the energy of a and h do not have the +same zero value. As is seen, certain arrangements of CO can lower +the energetic barrier that must be overcome to create an adatom. +However, it is the highest coverages where these higher-energy +configurations of CO will be more likely. } +\label{fig:SketchEnergies} +\end{figure} + +%Discussion +\section{Discussion} +We have shown that the classical potential models are able to model the initial reconstruction of the +Pt(557) surface upon CO adsorption as shown by Tao et al. \cite{Tao:2010}. More importantly, we +were able to observe features of the dynamic processes necessary for this reconstruction. + +\subsection{Diffusion} +As shown in Figure \ref{fig:diff}, for the Pt systems, there +is a strong trend toward higher diffusion constants as +surface coverage of CO increases. The drop for the 50\% +case being explained as double layer formation already +beginning to occur in the analyzed 40~ns, which lowered +the calculated diffusion rates. Between the parallel and +perpendicular rates, the perpendicular diffusion constant +appears to be the most important indicator of double layer +formation. As highlighted in Figure \ref{fig:reconstruct}, the +formation of the double layer did not begin until a nucleation +site appeared. And as mentioned by Williams et al.\cite{Williams:1991, Williams:1994}, +the inability for edges to cross leads to an effective repulsion. +This repulsion must be overcome to allow step coalescence. +A greater $\textbf{D}_\perp$ implies more step-wandering +and a larger chance for the stochastic meeting of two edges +to form the nucleation point. Upon that appearance, parallel +diffusion along the step-edge can help ``zipper'' up the double +layer. This helps explain why the time scale for formation after +the appearance of a nucleation site was rapid, while the initial +appearance of said site was unpredictable. + +\subsection{Mechanism for restructuring} +Since the Au surface showed no large scale restructuring throughout +our simulation time our discussion will focus on the 50\% Pt-CO system +which did undergo the doubling featured in Figure \ref{fig:reconstruct}. +Similarities of our results to those reported previously by Tao et al.\cite{Tao:2010} +are quite strong. The simulated Pt system exposed to a large dosage +of CO readily restructures by doubling the terrace widths and step heights. +The restructuring occurs in a piecemeal fashion, one to two Pt atoms at a +time, but is rapid on experimental timescales. The adatoms either break +away from the step-edge and stay on the lower terrace or they lift up onto +a higher terrace. Once ``free'', they diffuse on the terrace until reaching +another step-edge or rejoining their original edge. This combination of +growth and decay of the step-edges is in a state of dynamic equilibrium. +However, once two previously separated edges meet as shown in Figure 1.B, +this nucleates the rest of the edge to meet up, forming a double layer. +From simulations which exhibit a double layer, the time delay from the +initial appearance of a nucleation point to a fully formed double layer is $\sim$35~ns. + +A number of possible mechanisms exist to explain the role of adsorbed +CO in restructuring the Pt surface. Quadrupolar repulsion between adjacent +CO molecules adsorbed on the surface is one possibility. However, +the quadrupole-quadrupole interaction is short-ranged and is attractive for +some orientations. If the CO molecules are ``locked'' in a specific orientation +relative to each other, through atop adsorption for example, this explanation +gains some credence. The energetic repulsion between two CO located a +distance of 2.77~\AA~apart (nearest-neighbor distance of Pt) and both in +a vertical orientation, is 8.62 kcal/mol. Moving the CO apart to the second +nearest-neighbor distance of 4.8~\AA~or 5.54~\AA~drops the repulsion to +nearly 0 kcal/mol. Allowing the CO to rotate away from a purely vertical orientation +also lowers the repulsion. A minimum of 6.2 kcal/mol is reached at when the +angle between the 2 CO is $\sim$24\textsuperscript{o}, when the carbons are +locked at a distance of 2.77 \AA apart. As mentioned above, the energy barrier +for surface diffusion of a Pt adatom is only 4 kcal/mol. So this repulsion between +neighboring CO molecules can increase the surface diffusion. However, the +residence time of CO on Pt was examined and while the majority of the CO is +on or near the surface throughout the run, the molecules are extremely mobile, +with diffusion constants 40 to 2500 times larger, depending on coverage. This +mobility suggests that the CO are more likely to shift their positions without +necessarily the Pt along with them. + +Another possible and more likely mechanism for the restructuring is in the +destabilization of strong Pt-Pt interactions by CO adsorbed on surface +Pt atoms. To test this hypothesis, numerous configurations of +CO in varying quantities were arranged on the higher and lower plateaus +around a step on a otherwise clean Pt(557) surface. A few sample +configurations are displayed in Figure \ref{fig:lambdaTable}, with +energies at various positions along the path displayed in Table +\ref{tab:rxcoord}. Certain configurations of CO, cases B and D for +example, can have quite strong energetic reasons for breaking +away from the step-edge. Although the packing of these configurations +is unlikely until CO coverage has reached a high enough value. +These examples are showing the most difficult cases, immediate +adatom formation through breakage away from the step-edge, which +is why their energies at large distances are relatively high. There are +mechanistic paths where an edge atom could get shifted to onto the +step-edge to form a small peak before fully breaking away. And again, +once the adatom is formed, the barrier for diffusion on the surface is +negligible. These sample configurations help explain CO's effect on +general surface mobility and step wandering, but they are lacking in +providing a mechanism for the formation of double layers. One possible +mechanism is elucidated in Figure \ref{fig:lambda}, where a burrowing +and lifting process of an adatom and step-edge atom respectively is +examined. The system, without CO present, is nearly energetically +neutral, whereas with CO present there is a $\sim$ 15 kcal/mol drop +in the energy of the system. + +%lambda progression of Pt -> shoving its way into the step +\begin{figure}[H] +\includegraphics[width=\linewidth]{lambdaProgression_atopCO_withLambda.png} +\caption{A model system of the Pt(557) surface was used as the framework + for exploring energy barriers along a reaction coordinate. Various numbers, + placements, and rotations of CO were examined as they affect Pt movement. + The coordinate displayed in this Figure was a representative run. relative to the energy of the system at 0\%, there + is a slight decrease upon insertion of the Pt atom into the step-edge along + with the resultant lifting of the other Pt atom when CO is present at certain positions.} +\label{fig:lambda} +\end{figure} + + + + + +%breaking of the double layer upon removal of CO +\begin{figure}[H] +\includegraphics[width=\linewidth]{doubleLayerBreaking_greenBlue_whiteLetters.png} +\caption{(A) 0~ps, (B) 100~ps, (C) 1~ns, after the removal of CO. The presence of the CO + helped maintain the stability of the double layer and upon removal the two layers break + and begin separating. The separation is not a simple pulling apart however, rather + there is a mixing of the lower and upper atoms at the edge.} +\label{fig:breaking} +\end{figure} + + + + +%Peaks! +%\begin{figure}[H] +%\includegraphics[width=\linewidth]{doublePeaks_noCO.png} +%\caption{At the initial formation of this double layer ( $\sim$ 37 ns) there is a degree + %of roughness inherent to the edge. The next $\sim$ 40 ns show the edge with + %aspects of waviness and by 80 ns the double layer is completely formed and smooth. } +%\label{fig:peaks} +%\end{figure} + + +%Don't think I need this +%clean surface... +%\begin{figure}[H] +%\includegraphics[width=\linewidth]{557_300K_cleanPDF.pdf} +%\caption{} + +%\end{figure} +%\label{fig:clean} + + +\section{Conclusion} +In this work we have shown the reconstruction of the Pt(557) crystalline surface upon adsorption of CO in less than a $\mu s$. Only the highest coverage Pt system showed this initial reconstruction similar to that seen previously. The strong interaction between Pt and CO and the limited interaction between Au and CO helps explain the differences between the two systems. + +%Things I am not ready to remove yet + %Table of Diffusion Constants %Add gold?M % \begin{table}[H] @@ -427,77 +791,18 @@ linear fits to the mean squared displacement) are show % \end{tabular} % \end{table} -%Discussion -\section{Discussion} - -Mechanism for restructuring - -There are a number of possible mechanisms to explain the role of -adsorbed CO in restructuring the Pt surface. Quadrupolar repulsion -between adjacent CO molecules adsorbed on the surface is one -possibility. However, the quadrupole-quadrupole interaction is -short-ranged and is attractive for some orientations. If the CO -molecules are locked in a specific orientation relative to each other, -this explanation gains some weight. - -Another possible mechanism for the restructuring is in the -destabilization of strong Pt-Pt interactions by CO adsorbed on surface -Pt atoms. This could have the effect of increasing surface mobility -of these atoms. - -Comparing the results from simulation to those reported previously by -Tao et al. the similarities in the platinum and CO system are quite -strong. As shown in figure, the simulated platinum system under a CO -atmosphere will restructure slightly by doubling the terrace -heights. The restructuring appears to occur slowly, one to two -platinum atoms at a time. Looking at individual snapshots, these -adatoms tend to either rise on top of the plateau or break away from -the step edge and then diffuse perpendicularly to the step direction -until reaching another step edge. This combination of growth and decay -of the step edges appears to be in somewhat of a state of dynamic -equilibrium. However, once two previously separated edges meet as -shown in figure 1.B, this point tends to act as a focus or growth -point for the rest of the edge to meet up, akin to that of a -zipper. From the handful of cases where a double layer was formed -during the simulation, measuring from the initial appearance of a -growth point, the double layer tends to be fully formed within -$\sim$~35 ns. - -\subsection{Diffusion} -As shown in the results section, the diffusion parallel to the step edge tends to be much faster than that perpendicular to the step edge. Additionally, the coverage of CO appears to play a slight role in relative rates of diffusion, as shown in Table 4. Thus, the bottleneck of the double layer formation appears to be the initial formation of this growth point, which seems to be somewhat of a stochastic event. Once it appears, parallel diffusion, along the now slightly angled step edge, will allow for a faster formation of the double layer than if the entire process were dependent on only perpendicular diffusion across the plateaus. Thus, the larger $D_{\perp}$, the more likely a growth point is to be formed. One driving force behind this reconstruction appears to be the lowering of surface energy that occurs by doubling the terrace widths. (I'm not really proving this... I have the surface flatness to show it, but surface energy?) -\\ -\\ -%Evolution of surface -\begin{figure}[H] -\includegraphics[width=\linewidth]{ProgressionOfDoubleLayerFormation_yellowCircle.png} -\caption{The Pt(557) / 50\% CO system at a sequence of times after - initial exposure to the CO: (a) 258 ps, (b) 19 ns, (c) 31.2 ns, and - (d) 86.1 ns. Disruption of the 557 step edges occurs quickly. The - doubling of the layers appears only after two adjacent step edges - touch. The circled spot in (b) nucleated the growth of the double - step observed in the later configurations.} -\end{figure} - - -%Peaks! -\begin{figure}[H] -\includegraphics[width=\linewidth]{doublePeaks_noCO.png} -\caption{} -\end{figure} -\begin{figure}[H] -\includegraphics[width=\linewidth]{557_300K_cleanPDF.pdf} -\caption{} -\end{figure} -\section{Conclusion} - - -\section{Acknowledgments} +\begin{acknowledgement} Support for this project was provided by the National Science Foundation under grant CHE-0848243 and by the Center for Sustainable Energy at Notre Dame (cSEND). Computational time was provided by the Center for Research Computing (CRC) at the University of Notre Dame. - +\end{acknowledgement} \newpage \bibliography{firstTryBibliography} -\end{doublespace} +%\end{doublespace} + +\begin{tocentry} +%\includegraphics[height=3.5cm]{timelapse} +\end{tocentry} + \end{document}