1 |
gezelter |
3244 |
\section{Conclusions} |
2 |
|
|
\label{sec:conclusion} |
3 |
|
|
|
4 |
|
|
Our heat-transfer calculations have utilized the best current |
5 |
|
|
estimates of the interfacial heat transfer coefficient (G) from recent |
6 |
|
|
experiments. Using reasonable values for thermal conductivity in both |
7 |
|
|
the metallic particle and the surrounding solvent, we have obtained |
8 |
|
|
cooling rates for laser-heated nanoparticles that are in excess of |
9 |
|
|
10$^{13}$ K / s. To test whether or not this cooling rate can form |
10 |
|
|
glassy nanoparticles, we have performed a mixed molecular dynamics |
11 |
|
|
simulation in which the atoms in contact with the solvent or capping |
12 |
|
|
agent are evolved under Langevin dynamics while the remaining atoms |
13 |
|
|
are evolved under Newtonian dynamics. The effective solvent viscosity |
14 |
|
|
($\eta$) is a free parameter which we have tuned so that the particles |
15 |
|
|
in the simulation follow the same cooling curve as their experimental |
16 |
|
|
counterparts. From the local icosahedral ordering around the atoms in |
17 |
|
|
the nanoparticles (particularly Copper atoms), we deduce that it is |
18 |
|
|
likely that glassy nanobeads are created via laser heating of |
19 |
|
|
bimetallic nanoparticles, particularly when the initial temperature of |
20 |
|
|
the particles approaches the melting temperature of the bulk metal |
21 |
|
|
alloy. |
22 |
|
|
|
23 |
|
|
Improvements to our calculations would require: 1) explicit treatment |
24 |
|
|
of the capping agent and solvent, 2) another radial region to handle |
25 |
|
|
the heat transfer to the solvent vapor layer that is likely to form |
26 |
|
|
immediately surrounding the hot particle, and 3) larger particles in |
27 |
|
|
the size range most easily studied via laser heating experiments. |
28 |
|
|
|
29 |
|
|
The local icosahedral ordering we observed in these bimetallic |
30 |
|
|
particles is centered almost completely around the copper atoms, and |
31 |
|
|
this is likely due to the size mismatch leading to a more efficient |
32 |
|
|
packing of 5-membered rings of silver around a central copper atom. |
33 |
|
|
This size mismatch should be reflected in bulk calculations, and work |
34 |
|
|
is ongoing in our lab to confirm this observation in bulk |
35 |
|
|
glass-formers. |
36 |
|
|
|
37 |
|
|
The physical properties (bulk modulus, frequency of the breathing |
38 |
|
|
mode, and density) of glassy nanobeads should be somewhat different |
39 |
|
|
from their crystalline counterparts. However, observation of these |
40 |
|
|
differences may require single-particle resolution of the ultrafast |
41 |
|
|
vibrational spectrum of one particle both before and after the |
42 |
|
|
crystallite has been converted into a glassy bead. |
43 |
|
|
|